Substrate effects on phase formation and interfacial stability in superconducting vanadium silicide thin films

Abstract

Thin films of vanadium silicide (V-silicide) in the A15 cubic phase (V 3 Si) are promising for superconducting quantum devices due to their high transition temperature and potential compatibility with scalable semiconductor fabrication. However, solid-phase synthesis often yields secondary silicide phases that degrade performance. Here, in this study, we investigate the influence of substrate properties using two silicon-on-insulator architectures: one with a polycrystalline HfO 2 buried layer (group A) and the other with amorphous SiO 2 (group B). Both systems exhibit superconductivity consistent with V 3 Si formation, yet structural analysis reveals mixed-phase films in both cases. Crucially, only group A maintains an atomically sharp and chemically stable interface, a prerequisite for phase purity. Prolonged annealing in group A reduces the unwanted V 5 Si 3 phase but also leads to the emergence of Si-rich VSi 2 , likely due to localized substrate degradation. Preliminary atomic-resolution imaging suggests that HfO 2 crystallinity may promote local phase-selective nucleation. These findings highlight the importance of substrate design in promoting phase control and maintaining interfacial integrity in superconducting silicides.