UO2 microstructural evolutions induced by Ni, Mo, and W dopants for intentional forensics

Abstract

The concept of tagging nuclear fuel with a chemical barcode to enable forensics analysis across the nuclear fuel cycle is an area of active investigation, particularly to ensure fabrication viability without disrupting current fuel performance. This study explored the feasibility of using Ni, Mo, and W isotopic double-spikes as dopants in UO2 fuel from the perspective of fuel fabrication. Doped UO2 pellets were produced using conventional fuel fabrication processes, including powder mixing, sieving, pressing, and sintering in a reductive atmosphere. Two composition levels, 100 and 1000 ppm, were evaluated for each dopant element with isotopic double-spike configurations. For the Ni system, additional dopant concentrations of 250 and 500 ppm were produced with nonperturbed isotopic ratios. The results demonstrated that successful incorporation of Ni, Mo, and W double-spikes into UO2 pellets occurred with minimal shift in final density or dopant loss during pellet fabrication. Isotopic analysis confirmed the presence of the double-spike signature even when diluted with natural isotopic material in ratio of 1:5 in the fabrication process. Microstructural examinations revealed different impacts on grain size compared with undoped UO2. This study showed that Ni incorporation up to ∼500 ppm promoted moderate grain growth, whereas the Mo and W systems caused grain size reduction at all concentrations. Changes in the UO2 lattice parameter as a function of composition were detected exclusively for Ni up to 500 ppm, indicating that the Ni solid solution was the main factor for the observed grain growth. Insoluble (Mo and W) or supersaturated (Ni > 500 ppm) conditions produced grain size reduction. The Ni-doped pellets in the solution range resulted in a final microstructure within fuel specifications, demonstrating its potential benefits of employing complex dopant systems for potential nuclear forensic applications.