Development of High-Temperature Bonding Techniques to Enable High-Temperature Static or Dynamic Strain Measurements

Abstract

Current light-water nuclear reactors rely on a variety of different sensors and sensor applications to meet their structural health monitoring needs throughout the entirety of the reactor primary, secondary, and containment systems. Optical fiber–based sensor technologies could provide solutions to reduce the sensor system footprint while enhancing the measurement fidelity and spatial resolution by leveraging distributed monitoring techniques. Moreover, advanced reactors may require optical fiber–based sensors for structural health monitoring because their operating temperatures will exceed the limits of conventional transducers used to acquire dynamic strain or acoustic data in nuclear power plants. Therefore, this report describes experiments targeting the development of high-temperature bonding techniques that would allow for potentially long lengths of fibers to be bonded to metallic reactor components in advanced reactor systems. The high temperatures experienced within target application, next-generation nuclear reactors, necessitate a high-temperature resistant bond to limit the amount of tension on the fiber at the target application temperature. The primary bonding method investigated in this work is brazing; hot-rolling has also been investigated to a lesser extent. Both techniques are well-suited to bonding optical fibers to large reactor components such as primary coolant piping, pressure vessels, or heat exchangers. Optical frequency domain reflectometry was used to monitor the strain in metal-coated optical fibers before, during, and after the high-temperature bonding process. On select optical fibers that were successfully bonded, additional thermal cycling was performed to assess the extent to which the fiber remained bonded based on the expected thermal expansion of the test specimen material. The results of the various experiments yielded the following general conclusions: (1) brazing is a viable technique for bonding and allows significant compressive strain to be applied to the fiber at room temperature; (2) hot-rolling is a viable technique as well, which has been more optimized than the brazing technique for bonding, but less residual compressive strain has been observed with this technique; and (3) both techniques will need further development and optimization to demonstrate bonding of a long length of fiber that can provably operate at relevant temperatures for an advanced nuclear reactor application.