FCET Solid Oxide Fuel Cell Testing and Development (CRADA 526) (Final Report)

Abstract

Pacific Northwest National Laboratory (PNNL) tested electrolyte coatings from Fuel Cell Enabling Technologies, Inc. (FCET) for use in solid oxide fuel cells (SOFCs). The key technology held by FCET is a process to deposit thin layers of oxide materials, less than 1 μm in thickness. The range of possible materials that can be deposited with their method is broad, but this project focused on the gadolinium-doped ceria (GDC) and yttria-stabilized zirconia (YSZ) electrolytes for SOFCs. Thin, gas tight electrolyte membranes have been a long-sought target in SOFC research. The thinner the electrolyte, the lower the cell resistance, and the higher performance of the cell (or the lower the operating temperature). A YSZ thickness of 1 μm would be a step change from the state-of-the-art, tape-cast electrolytes (~10 μm). An in-house prototype SOFC stack from FCET was first tested. The sealing geometry of the prototype stack was determined to be problematic, and testing shifted to button cells. Anode-supported solid oxide electrolysis cell (SOEC) button cells without an electrolyte layer were produced at PNNL and sent to FCET for coating with electrolyte. Three cells were tested with a gadolinium-doped ceria (GDC) electrolyte applied via spin coating. GDC was chosen for its conductivity at lower temperatures than YSZ. All three cells failed during initial reduction under hydrogen at 600°C. Testing then shifted to YSZ, which is the standard SOFC electrolyte. Several button cells were coated with YSZ and examined with scanning electron microscopy (SEM). A promising coating of ~1 mm thickness was observed under SEM. A similarly coated button cell was tested and failed similarly to previous tests during reduction at 600°C. The YSZ coating appeared dense and uniform in SEM analysis. The roughness of the underlying Ni/YSZ anode is on the order of 1 μm, and that may have compromised the gas-tightness of the coating. Further development is warranted to understand and refine the coating process. Thin YSZ applied via this spin-coating technique could be used as a low-cost, drop-in replacement in large-scale SOFC manufacturing processes, improving cell performance and lowering the cost per watt of SOFCs.