Design and Production for Maximum Structural Efficiency With Respect to Fiber Orientation With Increased Understanding of Hybrid Fiber Flow Behavior

Abstract

Discontinuous fiber-reinforced thermoplastic composites have gained considerable attention in automotive, aerospace, and other industries, due to their high-rate of production combined with their ability to attain complex and intricate shapes. Among other high-rate thermoplastic manufacturing processes, injection-molding is one of the most common manufacturing methods due to fast production and high surface finishing of complex geometries. Fiber orientation in discontinuous fiber composites plays a pivotal role in determining the mechanical, electrical, and thermomechanical properties, underscoring the necessity to comprehend fiber orientation in injection molded parts. Among different fiber types, glass and carbon fibers are most common in the composite industries. The recent trend of hybrid composites comprising both glass fiber (GF) and carbon fiber (CF) is also gaining importance in the automotive industry. Hybrid fiber options allow designers to optimize the balance between glass and carbon fibers by leveraging the high durability and low cost of GF while the strength and lightweight properties of CF. Consequently, comparing the fiber oriented distribution (FOD) of injection molded composites containing GF, CF, and a hybrid of GF/CF is critical to investigating the local mechanical properties of intricate structures for high-end applications. In Phase I of this project, FOD in injection-molded panels with respect to distance from the gate was analyzed using X-ray computed tomography (X-CT) for GF, CF, and hybrid CF/GF (CGF) reinforced nylon 66. To understand the reason behind the FOD with different fiber types, computational fluid dynamics (CFD) and rheology were performed. Samples were extracted at three locations: near the gate, center, and opposite end. Thickness of the layers of typical skin-shell-core type FOD varies with fiber type and location. GF achieved flow direction alignment (in shell) earlier than viscous CF and CGF near the gate, whereas CF showed the highest flow-direction alignment at the center due to shear induced orientation. At the opposite end, GF experienced more backflow than others indicating faster mold filling owing to its lower viscosity. Hybrid CGF exhibited GF-dominated center and CF-dominated end region. The numerical model used to obtain FOD and rheological predictions for the CF and GF composites served to corroborate the trends observed in the experimental trials. The FOD responses across fiber types and location were reflected in their longitudinal and transverse properties. Only GF showed higher longitudinal modulus over transverse modulus near the gate attributed to rapid alignment, whereas CF and CGF exhibited opposite trend. However, fountain flow enhanced the longitudinal modulus over transverse modulus with the distance for all, particularly for CF. This study offers insights into mold filling behavior of different fibers which are critical in optimizing injection molding conditions for tailored final properties.