Ultra-selective CANAL Polymers for Hydrogen-based Membrane Separations after Long-Term Aging

Abstract

Hydrogen is a critically important molecule in the chemicals and energy industries, driving the need for efficient purification technologies such as membrane-based separations. However, polymer membranes often suffer from physical aging, leading to decreased gas permeability over time. This study leverages the unique aging behavior of contorted microporous polymers, synthesized via catalytic arene-norbornene annulation (CANAL) polymerization, to enhance molecular sieving for H 2 separations. While prior studies demonstrated a 1000% increase in H 2 /CH 4 selectivity with minimal permeability loss over 150 days, we extend this investigation to hyperaged (∼1 year) CANAL polymers and evaluate their performance under various conditions of industrial relevance. We report a remarkable 6100% increase in H 2 /CH 4 selectivity and a 2400% improvement in H 2 /N 2 selectivity, with only a 55% decline in H 2 permeability. These membranes exhibit excellent long-term stability in binary and ternary gas mixtures and at elevated temperatures. Additionally, extended aging enhances H 2 /CO 2 selectivity beyond the 2008 upper bound due to improved size-sieving. High-temperature permeation experiments and grand canonical Monte Carlo simulations reveal that H 2 permeability increases from 570 to 3500 barrer as the temperature rises from 35 °C to 190 °C, while H 2 /CO 2 selectivity declines from 14 to 3 due to the higher diffusion activation energy of CO 2 . Despite this tradeoff, hyperaged CANAL membranes maintain performance beyond the 200 °C upper bound, having selectivity–permeability performance comparable to many state-of-the-art membranes for H 2 /CO 2 separations. As a result, this study highlights the robustness and industrial viability of ultra-selective CANAL polymers for hydrogen purification, contributing to advancements in clean energy and sustainable separation technologies.