Heterostructured nano-catalysts with efficient metal-oxide interfaces unlock high-performance direct methanol protonic ceramic fuel cells

Abstract

Direct methanol protonic ceramic fuel cells (PCFCs) are attractive due to their low cost, convenient storage, and high volumetric energy density, as well as their suitability for transportation. However, the poor coking tolerance of conventional nickel-based anodes leads to their susceptibility to severe carbon deposition and significant deactivation after long-term exposure to hydrocarbons. Herein, we report a nano-catalyst of Ce 0.6 Ni 0.2 Cu 0.2 O 2 with a heterogeneous structure that is spontaneously reduced into a Ce 0.6 Ni 0.2-x Cu 0.2-x O 2-δ (CeNCO) oxide framework interfaced with a nano NiCu alloy (denoted as NC/CeNCO) under operating conditions, as confirmed by analyses of X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. A Ni-BaCe 0.7 Y 0.06 Yb 0.06 Zr 0.06 Hf 0.06 Gd 0.06 O 3-δ anode-supported PCFC employing the NC/CeNCO metal-oxide catalyst achieved a peak power density of 1.11 W cm −2 and operational stability of about 100 h at 700 °C when fueled by 35 % CH 3 OH-15 % H 2 O-50 % N 2 . In conclusion, the enhanced performance and coking resistance are attributed to the efficient interfaces of Ni, Cu, and ceria-based oxide in NC/CeNCO for CH 3 OH reforming, as confirmed by analyses of electrochemical performance and Raman spectroscopy with density functional theory calculations, revealing that these interfaces can enhance CH 3 OH activation and promote efficient OH-mediated carbon removal via COH intermediates.