HDG-1 Graphite Preirradiation Data Package Report

Rohrbaugh, David T [Idaho National Laboratory]; Windes, William E [Idaho National Laboratory] (ORCID:0000000188030885); Swank, W David [Idaho National Laboratory] (ORCID:0000000150138479)

DOE OSTI · 3018314

HDG-1 Graphite Preirradiation Data Package Report

Rohrbaugh, David T [Idaho National Laboratory]·Windes, William E [Idaho National Laboratory] (ORCID:0000000188030885)·Swank, W David [Idaho National Laboratory] (ORCID:0000000150138479)

View original source ↗Read source document ↗Export metadata ↓

Abstract

This report documents all pre-irradiation examination material-property measurement data for graphite specimens that are going to be used within the first high dose graphite (HDG) -1 irradiation capsule. The two new HDG capsules signify a major change to the AGC Experiment. HDG-1 and HDG-2 will replace the last two Advanced Graphite Creep (AGC) capsules (AGC-5 and AGC-6) which were designed to irradiate graphite at the extreme upper operational temperatures for a very-high-temperature reactor (VHTR) design, 1100°C. These very high temperature AGC-5 and AGC-6 capsules have been repurposed to re-irradiated specimens (from AGC-2, AGC-3, and AGC-4) at the lower temperatures of 600°C and 800°C. HDG-1 will be irradiated at 600°C and HDG-2 will be irradiated at 800°C. By re-irradiating the previous AGC specimens a total maximum neutron dose of around 15 dpa (displacements per atom) can be achieved for all major graphite grades at irradiation temperatures of 600°C and 800°C. Specimens in the HDG-1 capsule are made up of previously irradiated specimens from the AGC-2 capsule and unirradiated specimens prepared for the now discontinued AGC-5 capsule. Utilizing the irradiated specimens, a maximum neutron dose of around 15 dpa is anticipated. These new maximum dose levels will provide irradiated material property data over a total neutron dose range of 1-15 dpa at a temperature of 600°C when combined with the previous AGC-1 and AGC-2 irradiation data. This will provide quantitative data necessary for predicting the irradiation behavior and operating performance of new nuclear graphite grades for use within high temperature reactor designs. Similar to previous AGC test trains, HDG-1 includes the major graphite grades (IG-110, NBG-17, NBG-18, PCEA, and 2114) as well as adding the very fine-grain grade IG-430 which is of interest to the Molten Salt Reactor (MSR) designs. Also new to the HDG-1 capsule are 90 smaller geometry specimens designated as pencil specimens. These specimens take up only one third the space of a standard creep size specimen. This increased number of specimens will enhance property measurement statistics because they will provide 3 times the control specimen data at a position that would otherwise only have a single measurement.

Explore related subjects

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS Advanced Graphite Creep Graphite Preirradiation High Dose Graphite

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Rohrbaugh, David T [Idaho National Laboratory], Windes, William E [Idaho National Laboratory] (ORCID:0000000188030885), Swank, W David [Idaho National Laboratory] (ORCID:0000000150138479). 2025-04-08. HDG-1 Graphite Preirradiation Data Package Report. https://www.osti.gov/biblio/3018314

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Advanced Test Reactor Safety Basis Update for Gas-Cooled Experiments

The Advanced Test Reactor (ATR) supports neutron irradiation of several types of experiments. One such experiment type is referred to as a gas leadout. Gas leadout experiments actively flow gas through the experiment which allows for active temperature control. It also allows for in-situ data of the experiment. For example, fission gas migration through a fuel sample can be monitored via activity of the sweep gas. Historically, ex-pile equipment and fission product monitors were housed in shielded ATR cubicles. Due to other facility updates, cubicle space is no longer available for gas leadout experiment equipment. To support continued operation of gas leadout experiments, ATR completed a safety basis update that supports a new housing for leadout equipment that may process potentially contaminated gas. In addition to the structure and associated equipment, technical safety requirements regarding handling and storage of experiments needed to be revised to support fueled gas leadout experiments and associated outage configurations. The safety basis update addressed the full lifecycle of these experiments, including experiment movement and interim storage, and credible abnormal events such as failures or leaks in contaminated gas tubing in occupied areas. This paper discusses the completed analyses performed to support the safety basis update associated with gas leadout experiments, including thermal-hydraulic evaluation, probabilistic analysis, and dose consequence analyses.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2026

Synthesis, Characterization, and Testing of High-Lithium-Density Composite Breeders

Solid tritium breeder materials must first and foremost have sufficiently high concentrations of lithium to enable a plant-scale tritium breeding ratio greater than 1:1. However, in addition to lithium content, such breeder materials must also meet other performance metrics including high tritium release rates, thermal conductivities, and irradiation damage tolerance. Perhaps most importantly, tritium breeders must maintain their mechanical integrity during reactor operation so as to avoid degradation which can jeopardize the functionality of the tritium breeder blanket module, which in most designs takes the form of a pebble bed geometry. Unfortunately, the mechanical robustness of most lithium-bearing ceramics under investigation for fusion applications is often inversely related to the lithium atom density. For example, a material such as lithium oxide (Li2O), which has one of the highest lithium atom densities, has a much lower mechanical splitting strength than lithium metatitanate (Li2TiO3), though Li2TiO3 has less than half the lithium atom density of Li2O. This work seeks to provide an alternative to monolithic ceramic tritium breeders, in the form of metal-reinforced composite tritium breeders. Specifically, composite tritium breeders have been synthesized combining Li2O with various ferrous metal reinforcements via electric field assisted sintering (EFAS), also known as spark plasma sintering (SPS). As the metal reinforcement content is increased, metallic networks are observed, via electron microscopy and X-ray computed tomography, to form throughout the composite material. Through destructive mechanical testing, even dilute metal reinforcement loading enables drastic mechanical strength improvements over pure Li2O while higher loadings give rise to quasi-ductile behavior and higher ultimate strengths than Li2TiO3 – while still maintaining a higher density of lithium atoms than Li2TiO3 and many other breeder candidates. In addition to microstructural characterization and mechanical testing, thermal property measurements and hydrogen permeability testing are underway to further assess the suitability of such composites for fusion reactor applications.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2026

Results of the AGR-5/6/7 UCO TRISO fuel irradiation test in the Advanced Test Reactor

AGR-5/6/7 was the last in a series of irradiation experiments sponsored by the U.S. Department of Energy in support of the development and qualification of TRISO coated particle fuel for use in a high-temperature gas-cooled reactor. This experiment was conducted to verify the performance of the reference-design TRISO-coated low-enriched UCO fuel for modular high-temperature gas-cooled reactor normal operating conditions and to explore fuel performance at temperatures substantially beyond those typical of normal operation. A total of 194 UCO fuel compacts in five capsules were irradiated in the Advanced Test Reactor for 360.9 effective full-power days, achieving final burnup ranging from 5.66% to 15.26% fissions per initial heavy metal atom and fast neutron fluence ranging from 1.62 × 10 25 to 5.55 × 10 25 n/m 2 (E > 0.18 MeV). Calculated time-averaged fuel temperatures ranged from 467 °C to 1432 °C, with a peak fuel temperature of 1536 °C. During the first five irradiation cycles (∼180 effective full-power days), 85m Kr fission gas release-rate-to-birth-rate ratios were 10 −7 –10 −6 , indicating no particle failures. Near the end of the sixth cycle, a substantial number of in-pile particle failures occurred in Capsule 1. The fission gas release from this capsule impacted the readings from the other four capsules and led to unreliable fission gas release measurements for all capsules during the last four cycles. A preliminary post-irradiation examination of Capsule 1 fuel and internal components revealed the in-pile particle failures resulted from operational issues with the capsule, not subpar performance of the fuel particles.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗