Enhanced coercivity in Fe5C2/SiO2 core/shell nanocrystals

Joshi, Pramanand [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000322456618); Abbas, Hur [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000264822527); Karki, Tej Raj [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0009000215121502); Mohapatra, Jeotikanta [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000151968626); Liu, Xubo [Critical Materials Innovation Hub, Division of Critical Materials, Ames National Laboratory, US DOE 2 , Ames, Iowa 50011,] (ORCID:0000000225580959); Liu, J. Ping [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000179786357)

doi:10.1063/9.0001042

DOE OSTI · 3021616

Enhanced coercivity in Fe5C2/SiO2 core/shell nanocrystals

Joshi, Pramanand [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000322456618)·Abbas, Hur [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000264822527)·Karki, Tej Raj [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0009000215121502)·Mohapatra, Jeotikanta [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000151968626)·Liu, Xubo [Critical Materials Innovation Hub, Division of Critical Materials, Ames National Laboratory, US DOE 2 , Ames, Iowa 50011,] (ORCID:0000000225580959)·Liu, J. Ping [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000179786357)

View original source ↗Read source document ↗Export metadata ↓

Abstract

Rod-shaped Fe5C2 and core/shell Fe5C2/SiO2 nanocrystals were synthesized via a solution-based chemical method. Structural analysis confirmed the monoclinic phase of Fe5C2 with space group C2/c. Zero-field-cooling (ZFC) and field-cooling (FC) magnetization curves revealed distinct magnetic behaviors: uncoated Fe5C2 exhibited a low-temperature FC plateau indicative of strong dipolar interactions, while Fe5C2/SiO2 showed a monotonic increase in FC magnetization, suggesting reduced dipolar interactions due to SiO2 surface passivation. Isothermal remanent magnetization (IRM) and DC demagnetization (DCD) measurements supported this trend, with δM plots confirming weaker dipolar interactions in the coated sample. Bloch’s law fitting of temperature-dependent saturation magnetization showed a smaller Bloch’s constant for pure Fe5C2 and a larger value for Fe5C2/SiO2, reflecting enhanced surface disorder and reduced exchange coupling in the latter. Notably, Fe5C2/SiO2 demonstrated increased coercivity, attributed to decreased dipolar interaction and elevated surface anisotropy. Kneller’s law fitting yielded higher blocking temperatures for Fe5C2 (476 K) than Fe5C2/SiO2 (456 K), highlighting the impact of dipolar interactions on magnetic relaxation. These findings illustrate how SiO2 coatings effectively modulate dipolar interactions and enhance coercivity in Fe5C2 nanocrystals.

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Joshi, Pramanand [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000322456618), Abbas, Hur [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000264822527), Karki, Tej Raj [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0009000215121502), Mohapatra, Jeotikanta [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000151968626), Liu, Xubo [Critical Materials Innovation Hub, Division of Critical Materials, Ames National Laboratory, US DOE 2 , Ames, Iowa 50011,] (ORCID:0000000225580959), Liu, J. Ping [Department of Physics, University of Texas at Arlington 1 , Arlington, Texas 76019,] (ORCID:0000000179786357). 2026-02-09. Enhanced coercivity in Fe5C2/SiO2 core/shell nanocrystals. https://doi.org/10.1063/9.0001042

Cite the original work for its findings. Save a collection to share your selection of sources.