Point defects and impurities in fluorite PuO 2

Abstract

The native surface oxide of plutonium plays a critical role in ensuring the stability and safe storage of the underlying metal; consequently, understanding the role of defects and impurities in determining the properties of the oxide layer is critical. Here, in this study, we use hybrid density-functional theory calculations to evaluate the electronic structure and defect chemistry of PuO 2 , the most stable of the native oxide phases, including both native and extrinsic defects. We find that oxygen vacancies (𝑉 O ) form readily in PuO 2 , as do polarons. Electron polarons (𝜂 − ) are the lowest-energy acceptor species in PuO 2 , while the charge compensating donor species will shift from 𝑉 O under O-poor conditions to hole polarons (𝜂 + ) under O-rich conditions. Nitrogen and fluorine can substitute readily for oxygen atoms under O-poor conditions, while fluorine can also incorporate in an interstitial configuration (F$^−_i$) under more O-rich conditions. Carbon and chlorine incorporation in PuO 2 will be very limited. We also evaluate the kinetic barriers for oxygen-related defects, which we find to diffuse readily when present. Our results provide valuable insights into the critical role and variable chemistry of point defects and impurities in PuO 2 , which in turn have important implications for the safe storage of the underlying metal layer. In short, exposure of freshly prepared plutonium to reactive nitrogen- and fluorine-containing contaminants should be avoided, while carbon- or chlorine-containing contaminants are less likely to incorporate readily into the oxide.