Resilient high-temperature reverse osmosis desalination membranes

Abstract

Conventional thin-film composite (TFC) reverse osmosis (RO) membranes experience irreversible performance loss at high temperatures, restricting their use in industries with high-temperature streams, including oil and gas, pharmaceuticals, electronics, power generation, food production, and hybrid desalination plants. However, the mechanisms driving the performance decline of TFC membranes at high temperatures remain poorly understood. Herein, we combine controlled experiments, molecular dynamics simulations, and micromechanical modeling to elucidate TFC failure mechanisms and to evaluate thermally resilient thin-film cross-linked (TFX) composite membrane. Upon exposure to elevated temperatures (>60°C), salt rejection of TFC dropped from ~99 to <90%, with irreversible structural damage in the polysulfone layer, confirmed by scanning electron microscopy. In contrast, the TFX membrane maintained ~99% salt rejection and showed no signs of physical degradation up to 80°C. Our combined analyses revealed that TFC membrane failure arises from irreversible pore expansion in the thermoplastic polysulfone support, leading to polyamide film rupture and delamination. TFX membranes resist thermal deformation, enabling ultrahigh-temperature RO desalination and water reuse.