ATF Cladding Mechanical Properties Report: Capability Demonstration

Abstract

This report documents mechanical testing capability demonstration activities performed in fiscal year (FY)2025 at Oak Ridge National Laboratory(ORNL)on chromium-coated (Cr-coated) and uncoated advanced zirconium alloy claddings irradiated in the High Flux Isotope Reactor (HFIR) to approximately 4 displacements per atom (dpa), corresponding to ~13GWd/t burnup. Specimens were prepared in axial tension (ATT) and ring tension (RTT) geometries, and passive silicon carbide(SiC)thermometry (TM) was employed to determine irradiation temperatures, which averaged 38–43 °C below the 330 °C design target. Mechanical testing at ambient temperature demonstrated the expected irradiation-induced hardening, with yield strength(YS)and ultimate tensile strength(UTS)values increasing substantially relative to unirradiated counterparts. However, this strengthening was accompanied by a reduction in ductility, as indicated by lower uniform and total elongations(UE and TE). Both coated and uncoated claddings exhibited similar mechanical response, though Cr-coated specimens showed surface cracking perpendicular to the loading direction, attributable to the hardness mismatch between the coating and substrate. Fracture in all cases remained ductile, and no coating spallation was observed following HFIR irradiation. Complementary efforts were directed toward the fabrication of test specimens from commercially irradiated cladding (rod 47I, ~31.1 GWd/t average burnup). Axial sectioning and computer numerical control(CNC)machining successfully produced ATT geometries suitable for benchmarking against HFIR-irradiated specimens. This capability enables direct comparison of cladding behavior between test reactor and commercial reactor environments, thereby supporting the validation of HFIR as a surrogate irradiation platform for accident tolerant fuel (ATF) development. Once HFIR irradiations are completed in FY26,the relevant comparison tests will be completed. Collectively, the FY 2025 PIE campaign has provided mechanical performance data for irradiated advanced claddings The demonstrated capabilities support the framework for mechanical testing and further evaluations in subsequent years. These efforts will represent an important contribution toward the licensing and deployment of Cr-coated zirconium alloy cladding as a near-term ATF solution.