Multiscale Cryo Electron Microscopy Reveals Interfacial Degradation and Stabilization in Battery Electrodes

Abstract

Electrochemical interfaces are dynamic systems, evolving based on their local environment and reactant surface structures. The electrode-electrolyte interface in Li-ion batteries can be protective, limiting parasitic reactions with the electrolyte to passivate the surface [1]. Additionally, this interphase has an impact on the Li-ion transport through that layer based on its composition, bonding environment, and thickness. These parameters are challenging to collect and may vary depending on the electrode surface site investigated relative to its spatial position in a coin cell. This study will detail a multiscale cryogenic electron microscopy approach where millimeter-scale cross-sections through the coin cell batteries were made using a cryogenic stage within a fs-laser plasma focused ion beam (laser PFIB) with complementary energy dispersive X-ray spectroscopy able to detect variations in the composition at electrode interfaces [2]. Microscale cross-sectioning and lamella sample preparation of battery electrodes was conducted at the Center for Integrated Nanotechnologies using a Ga-ion focused ion beam (FIB) with air-free and cryo-transfer [3], followed by nanoscale mapping of composition and bonding within the CEI through cryo-scanning transmission electron microscopy (cryo-STEM) electron energy loss spectroscopy [4]. This multiscale approach enabled identification of millimeter-scale features of a battery stack with visualization of degradation in electrodes such as cracks in cathode particles, gas evolution, and SEI evolution; microscale interfacial characteristics, such as heterogeneity in the SEI or barrier layer and identification of electrolyte networks to the electrode surfaces; and nanoscale measurement of the CEI thickness, mapping of transition metal bonding within the cathode particles to identify loss of active materials, and identification of beneficial electrolyte additives incorporated into the CEI structure. This multiscale approach allows for a statistical understanding of the primary mechanisms and parasitic degradation pathways that impact performance by limiting the ion transport pathways within Li+ batteries.