Thermal Gradient Effects on Redox Evolution and Volatility-Driven Fractionation in Ternary U/Ce/Cs Condensates

Abstract

Understanding how thermal history influences redox evolution and chemical fractionation is essential for characterizing high-temperature condensation in complex materials, including nuclear debris. Here, we tested the hypothesis that distinct thermal regimes in a plasma flow reactor influence redox pathways and elemental partitioning in ternary U/Ce/Cs systems. A configurable plasma flow reactor was modified with an external tube furnace to impose two distinct thermal gradients: continuous ambient cooling and a furnace-assisted thermal hold-up near 1400 K followed by rapid cooling. Transmission electron microscopy characterized phase identity, morphology, and nanoscale element distributions, while inductively coupled plasma-mass spectrometry quantified bulk elemental ratios. Across both thermal regimes, uranium and cerium condensed as UO 2 and CeO 2 as dominant refractory oxide products. Uranium partially oxidized to α-UO 3 during extended ambient cooling, while furnace-assisted hold-up preserved UO 2 and produced partial reduction of cerium to Ce 2 O 3 . Cesium remained volatile upstream and condensed later in the reactor, forming Cs 2 O and Cs-uranate phases with the highest incorporation after thermal hold-up. Bulk ICP-MS measurements supported these observations. U/Ce ratios remained comparatively stable and Cs displayed delayed and apparent transient enrichment that matched the nanoscale measurements. This integrated approach provides a quantitative method for linking thermal gradients to redox evolution and volatility-driven fractionation. These results show how the plasma flow reactor can identify where equilibrium descriptions remain adequate and where kinetic effects from residence time and temperature history must be considered when interpreting condensation behavior in multicomponent systems.