Degradation science: Integrating modeling and experiments to predict localized corrosion processes (Annual Progress Report)

Abstract

Additively manufactured (AM) eutectic high-entropy alloys (EHEAs), such as nano-lamellar AlCoCrFeNi 2.1 , have excellent strength, ductility, and wear resistance even at elevated temperatures, but their corrosion behavior in aggressive acids at different length scales remain poorly understood. This work investigates the corrosion behavior of laser powder bed–fused (L-PBF) AlCoCrFeNi 2.1 as a function of annealing temperatures, probing degradation mechanisms from nanoscopic to macroscopic length scales. The alloy is dual phase consisting of a ductile FCC L1 2 phase and a high-strength BCC B2 phase. Rapid solidification during L-PBF produces a far-from-equilibrium nano-lamellar structure with nearly homogeneous elemental distribution, which tends to evolve upon annealing toward Cr/Co/Fe-enriched FCC and Al/Ni-enriched B2. Three conditions were studied: as-printed, 600 °C/5 h, and 1000 °C/1 h, over which B2 lamellae coarsen, lamellar spacing increases, and elemental segregation becomes more prominent. Microstructure and chemistry were characterized by scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS), while in-situ electrochemical atomic force microscopy (EC-AFM) was used to link early (<5 h) local dissolution to microstructure after exposure in sulfuric acid. EC-AFM highlights preferential dissolution of the BCC/B2 phase where the surrounding matrix is Cr-depleted and directly quantifies the dissolution rates within individual phases, tracks the transition from early nano-scale attack to partial repassivation, to correlate height differences with current and impedance responses. To monitor longer-term behavior (up to 96 h), ex-situ AFM, SEM, and confocal imaging were combined with conventional bulk electrochemical tests, bridging nanoscale observations to micro/meso-scale damage morphologies. At the meso-scale, the deepest dissolution channels align with the build-direction lamellae and melt-pool boundaries, indicating that printing directionality guides the propagation of these localized corrosion sites. Annealing modifies corrosion by restructuring BCC/FCC phase fractions, lamellar spacing, and Cr/Al segregation, thereby changing the cathode/anode ratio and passive film stability. The results clarify how as-printed and annealed nano-lamellar architectures differ in their susceptibility to selective dissolution; how elemental segregation competes with residual stresses along the build direction. With these insights, future work will use CALPHAD-guided alloy modification to stabilize higher Cr contents in the B2 phase while retaining a dominant FCC+B2/BCC microstructure, with the goal of designing mechanically robust, corrosion-resistant EHEAs for safety-critical applications to leverage the LLNL’s broader national and global security mission.