Hollow-structured Ni-N-C catalysts for highly selective CO 2 electroreduction

Abstract

Atomically dispersed single-atom catalysts have emerged as promising non-precious catalyst alternatives to expensive Ag and Au catalysts for electrochemical CO 2 reduction reaction (CO 2 RR). In particular, nickel-nitrogen-carbon (Ni-N-C) catalysts have demonstrated a high faradaic efficiency (FE) toward CO formation at low overpotentials. Nonetheless, the exact nature of Ni active sites under CO 2 RR remains elusive and conventional Ni-N-C catalysts are limited by microporosity and low density of Ni single atoms, hindering performance in CO 2 electrolyzers. Here, we report the synthesis of hollow-structured Ni-N-C ( hs -Ni-N-C) catalysts via a post-synthesis modification (PSM) strategy using partial ligand exchange of 2-methylimidazole with 3-amino-1,2,4-triazole. This approach enables the formation of a hollow structure, resulting in more than a twofold increase in Ni atom density compared to regular Ni-N-C (r-Ni-N-C). In a zero-gap CO 2 electrolyzer, the optimized hs -Ni-N-C allows for achieving an FE CO of 97% at a current density of > 100 mA cm⁻ 2 , while maintaining high CO selectivity with stable performance over 100 h at 2.5 V. hs-Ni-N-C shows a more than sevenfold increase in the CO partial current density relative to r-Ni-N-C resulting from the combined effects of a higher density of Ni single-atom sites, improved kinetics, and lower transport resistance under the operating conditions, as indicated by electrochemical impedance spectra and distribution of relaxation times analysis. Operando high energy-resolution X-ray absorption spectroscopy (XAS) reveals that atop-bonded CO on Ni single sites induces dynamic transformations of the Ni–N coordination environment, leading to a symmetric coordination structure of hs -Ni-N-C. Under CO 2 RR, the catalysts undergo a more pronounced structural change and form a minor fraction of Ni nanoparticles. Density functional theory calculations are consistent with the XAS results and provide molecular insights showing that the interplay between protonation and CO adsorption leads to adsorbate-induced restructuring of the Ni single atom. This work demonstrates the synergistic role of hollow structure and high-density Ni atoms in governing CO 2 RR selectivity and provides mechanistic insights into the structural dynamics of single-atom catalysts under operating conditions.