Linking microstructure to creep behavior in vertically and horizontally built LPBF Haynes 282 compared with wrought material via θ -projection

Abstract

Laser Powder Bed Fusion (LPBF) has emerged as a promising route for fabricating intricate geometries in high-performance alloys. Haynes 282 (H282) is a strong candidate for applications such as heat exchangers or engines due to its excellent creep strength and thermal stability; however, the long-term creep behavior of LPBF-processed H282 remains poorly understood. In this study, the θ -projection method is used to analyze and extrapolate the creep behavior of vertically built LPBF, horizontally built LPBF, compared to wrought H282 tested at 816 °C. Vertically built LPBF H282 exhibits the lowest minimum creep rate (MCR), while the horizontally built condition shows a higher MCR comparable to that of wrought H282. Despite these differences, both LPBF conditions exhibit significantly shorter rupture life and reduced rupture strain than the wrought material, with the most severe degradation observed in the horizontal builds, consistent with an earlier onset of tertiary creep and accelerated strain-rate evolution. Microstructural characterization reveals that both LPBF and wrought H282 exhibit abundant twin-related boundary character; however, their grain boundary topologies differ markedly. The wrought alloy contains a higher fraction of low-angle grain boundaries and continuous twin lamellae, whereas the LPBF microstructure is characterized by a suppressed low-angle boundary population and fragmented twin-related boundaries embedded within irregular high-angle grain boundary networks. Fractographic analysis further reveals predominantly intergranular cracking in LPBF H282, accompanied by grain-boundary-decorated carbides, Al 2 O 3 inclusions, and high-aspect-ratio pores. These results demonstrate that grain boundary topology, rather than minimum creep rate alone, plays a critical role in governing creep damage accumulation and rupture behavior in LPBF and wrought H282.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Yi, Yu-Tsen [Carnegie Mellon Univ., Pittsburgh, PA (United States)] (ORCID:0000000170392933), Lamprinakos, Nicholas [Carnegie Mellon Univ., Pittsburgh, PA (United States)], Chen, Xiang [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000286625209), Kombaiah, Boopathy [Idaho National Laboratory (INL), Idaho Falls, ID (United States); Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000157062534), Rollett, Anthony D. [Carnegie Mellon Univ., Pittsburgh, PA (United States)]. 2026-05-25. Linking microstructure to creep behavior in vertically and horizontally built LPBF Haynes 282 compared with wrought material via θ -projection. https://doi.org/10.1016/j.msea.2026.150450

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

High-temperature mechanical properties of a γ′-strengthened Co-based superalloy designed for additive manufacturing

GammaPrint®-700 is a recently developed high γ′ (∼70% volume fraction) CoNi-based superalloy designed to combine high-temperature mechanical performance with laser powder bed fusion processability. Room-temperature yield strength ranged from 610 to 658 MPa and increased to 661 MPa (longitudinal) and 730 MPa (transverse) at 760 °C. The creep behavior compared favorably to high-γ′ Ni-based superalloys manufactured via laser powder bed fusion such as Incoloy® 939 and Inconel® 738LC. In-situ neutron diffraction data measured during creep revealed that plastic deformation was largely localized to the γ phase at 760 °C, allowing the γ’ phase to elastically compensate and maintain creep strain resistance. Furthermore, at 900 °C, this load sharing behavior was weakened, contributing to accelerated creep rate and rupture.

Creep↗

Creep behavior of high-entropy alloys: A critical review

High-entropy alloys (HEAs) have been extensively investigated during the last two decades. While substantial progress has been made in understanding their phase stability, microstructure, and deformation mechanisms at room and cryogenic temperatures, the long-term creep behavior (>100 h) of HEAs at high temperatures (>0.6 T m , where T m is the melting temperature) remains relatively underexplored. This knowledge gap is critical, as many engineering applications, including those for power generation and propulsion, require materials with good creep resistance to maintain structural integrity over extended service lifetimes. This review provides a focused and critical assessment of the current understanding of high-temperature deformation and creep behavior of HEAs, with particular attention paid to face-centered cubic HEAs and body-centered cubic refractory HEAs. The underlying deformation mechanisms governing their creep response and the influence of phase stability at elevated temperatures are examined in detail. Recent studies reveal mechanistic differences between HEAs and conventional dilute alloys that do not always lead to improved creep resistance belying their initial promise. Based on these findings, we discuss the challenges in designing HEAs for high-temperature structural applications and outline future research directions that may lead to creep-resistant HEAs.

Creep↗

Effect of stress on Laves phase precipitation in creep ruptured Grade 92 ferritic martensitic steel characterized by a novel accessible method

At high temperature conditions relevant to fossil and nuclear energy plants, Laves phase (Fe 2 X, X=Mo, W) precipitation is observed in common ferritic martensitic (FM) structural steels, with various reported effects on creep behavior. Despite being valuable metrics to correlate with mechanical properties and other precipitate phases, the volume fraction and number density of Laves phase precipitates has been difficult to quantify accurately using common techniques such as transmission electron microscopy (TEM) due to the relatively large size (∼0.25 μm) and low number density (∼10 11 cm −3 ) of Laves precipitates. Here, to address this characterization challenge, we developed and demonstrated a high-throughput and widely accessible method to quantify the volume fraction and number density of the Laves phase based on scanning electron microscope (SEM) images with a backscattered electron signal and the information depth (ID) of backscattered electrons. We applied this new technique in creep ruptured Grade 92 FM steel to study the effect of Laves phase on creep properties and determine the influence of stress on Laves phase precipitation. The quantitative accuracy of the SEM-based volume fraction and number density values was verified using synchrotron high energy X-ray diffraction and serial sectioning tomography. Stress did not significantly affect the Laves phase size or volume fraction during creep testing at 550 – 650°C and stress levels of 90 – 260 MPa (vs. unstressed conditions). Conversely, a moderate but statistically significant stress-enhanced increase in Laves phase number density, corresponding to an increase in nucleation rate, occurred during creep exposure above 110 MPa.

Creep↗