Mg and native defects in cubic silicon carbide from first principles

Abstract

The diffusion of Mg defects in 3C-SiC is studied using the density functional theory. Mg has the highest burn-in rate as a transmutant in 3C-SiC when it is placed in high-energy neutron irradiation environment of a fusion reactor. The presence and evolution of transmutant defects impact thermal and mechanical properties of this important structural material. This study is focused on understanding the structure, stability, and evolution of Mg defects and the interaction of Mg with native defects in 3C-SiC. Our calculations of diffusion coefficients for different Mg defects suggest that Mg is likely to diffuse faster in pristine 3C-SiC than in the damaged one, in agreement with earlier experimental observations.