Tailored Silicone Network Architecture for Ultimate Mechanical Reinforcement

Abstract

Hydrosilylation cured silicone elastomers are subject to reaction inefficiency, leading to incomplete and non-uniform crosslink networks, restricting the potential of mechanical reinforcement. This work investigates pre-synthesized, functional PDMS architectures as additives to improve ultimate mechanical performance relative to conventional single-step curing. Three custom, functional structures were prepared: a partially crosslinked PDMS scaffold (Structure A), a bottle-brush PDMS (Structure B), and a star-shaped PDMS derived from an MQ resin (Structure C). Rheological characterization was used to identify the ultimate design space and proper stoichiometric ratio for Structure A, and confirm successful formation of all structures for suitable incorporation into a base silicone formulation at 30wt%. Mechanical tests indicated that all three structures increased in ultimate tensile strength relative to their single-step counterparts, with Structure A providing additional improvements to toughness (432 vs. 258 kJ/m3) and ultimate elongation (158 vs. 115%). Furthermore, Structure B remained very soft in the unfilled state, while Structure C provided hardness (23 vs. 18 Shore A) and stiffness (780 vs. 420 kPa Young’s modulus) increases. In silica filled systems, Structure A retained increased strength but reduced elongation, while Structure B indicated strong reinforcement in terms of strength, toughness, and stiffness. Thermal analysis on the cure profiles of these materials suggested that pre-formation of network architectures enable a more complete reaction than a single-step process (15.9 vs. 15.1 J/g). Ultimately, these results indicate that tailoring PDMS architecture before the final cure can improve ultimate mechanical properties via improved network development in silicone elastomers. Furthermore, this work offers a promising strategy for designing higher-performance, more tunable silicone formulations.