Probing Operando Electrochemical Strain Generation in α-NaFeO 2 Composite Cathodes during Cycling of Na-Ion Batteries

Abstract

The transition metal oxide (TMO) cathodes in Na-ion batteries suffer from low-capacity retention. Chemo-mechanical instabilities lead to the deterioration of the electrochemical performance of TMO cathodes in Li-ion batteries. However, there is not much known about the chemo-mechanical instabilities in the TMO cathodes for Na-ion batteries. Understanding the governing forces behind the interplay between the electrochemical performance and mechanical stability in TMO cathodes is critical for the development of Na-ion batteries. Here, we synchronize the digital image correlation (DIC) technique with electrochemical analysis to capture the real-time deformation behavior of the α-NaFeO 2 cathodes during cycling. When the charge cutoff voltage is 3.6 V, the cathode experiences reversible deformations (except for the first cycle). There is negative strain (shrinkage) generation during Na extraction and positive strain (expansion) generation during the subsequent Na insertion. A detailed analysis of the potential-dependent strain rate evolution points out complicated phase transformations and nonequilibrium conditions in the α-NaFeO 2 cathodes during cycling. When the charge cutoff voltage was increased to 4.2 V, there was a rapid capacity loss and large plastic deformations in the α-NaFeO 2 cathodes. We provide an in-depth discussion about the possible mechanisms behind the chemo-mechanical instabilities in the α-NaFeO 2 . In conclusion, the correlation is critical to develop material-based strategies to mitigate instability mechanisms in TMO cathodes for Na-ion batteries.

Keep this discovery

BibTeXRIS

Wable, Minal [University of Maryland Baltimore County (UMBC), Baltimore, MD (United States)], Park, Jehee [Argonne National Laboratory (ANL), Argonne, IL (United States); Hanbat National University, Daejeon (Korea, Republic of)] (ORCID:0009000078175351), Lee, Eungje [Argonne National Laboratory (ANL), Argonne, IL (United States)] (ORCID:0000000336471595), Johnson, Christopher S. [Argonne National Laboratory (ANL), Argonne, IL (United States)] (ORCID:0000000343576889), Çapraz, Ömer Özgür [University of Maryland Baltimore County (UMBC), Baltimore, MD (United States)] (ORCID:0000000223964748). 2025-12-08. Probing Operando Electrochemical Strain Generation in α-NaFeO 2 Composite Cathodes during Cycling of Na-Ion Batteries. https://doi.org/10.1021/acs.chemmater.5c02288

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

Manipulating Na/TM Ratio‐Driven Structural Heterogeneity of O3‐NaNi 1/3 Fe 1/3 Mn 1/3 O 2 Cathode for High‐Voltage Sodium‐Ion Batteries

The stability of O3-type NaNi 1/3 Fe 1/3 Mn 1/3 O 2 under high-voltage cycling is dictated by how synthesis encodes lattice strain and redox heterogeneity. Here, in this study, the role of Na:TM stoichiometry is systematically resolved by tuning the NaOH:precursor ratio during solid-state synthesis. The stoichiometric condition (Na:TM = 1.00) yields minimized microstrain, enabling uniform O3–P3 phase evolution and homogeneous multi-metal redox with preserved octahedral symmetry. In contrast, Na-excess compositions inherit disordered intermediates and heterogeneous distortion fields that trigger abrupt multiphase transitions and promote localized charge redistribution. In situ XRD captures the divergence in phase-transition pathways, TXM resolves particle-level redox heterogeneity, and XANES corroborates a stronger and more reversible Fe redox contribution at stoichiometry, shifting to diminished Fe participation and spatially inhomogeneous redox at higher Na content. These results establish Na:TM stoichiometry as a critical synthesis parameter controlling both structural coherence and redox stability. Electrochemically, the stoichiometric composition exhibits smooth voltage profiles with minimal polarization growth and retains nearly 80% of its initial capacity after 100 cycles even at an extended 4.2 V cutoff, whereas Na-excess compositions show significantly reduced initial coulombic efficiency and rapid voltage fade. Precise stoichiometric tuning provides a scalable route to defect-suppressed O3 frameworks, enabling structurally resilient, high-voltage sodium-layered cathodes.

36 MATERIALS SCIENCE

Mitigating Sodium Ordering for Enhanced Solid Solution Behavior in Layered NaNiO 2 Cathodes

The O-type layered nickel oxides suffer from undesired cooperative Jahn–Teller distortion stemming from Ni 3+ ions and undergo multiple biphasic structural transformations during the insertion/extraction of large Na + ions, posing a significant challenge to stabilize the structural integrity. We present here a systematic investigation of the impact of substituting 5 % divalent (Mg 2+ ) or trivalent (Al 3+ or Co 3+ ) ions for Ni 3+ to alleviate Na + ion ordering and perturb the Jahn–Teller effect to enhance structural stability. Here, we gauge a fundamental understanding of the Mg−O and Na−O or Mg−O−Na bonding interactions, noting that the ionicity of the Mg−O bond deshields the electronic cloud of oxygen from Na + ions. Furthermore, calculations of the Van Vleck distortion modes reveal a relaxation of NiO 6 octahedra from Jahn–Teller distortion and a reduced electron density at the interlayer with Mg 2+ substitution. Long-range (operando X-ray diffraction) and short-range (magic angle spinning nuclear magnetic resonance) structural analyses provide insights into reduced ordering, allowing a stable continuous solid solution. Overall, Mg-substitution results in a high-capacity retention of ~96 % even after 100 cycles, showcasing the potential of this strategy for overcoming the structural instabilities and enhancing the performance of sodium-ion batteries.

25 ENERGY STORAGE

Probing the role of local tunnel variations in early-stage lithiation of α-MnO₂ nanowires via in situ TEM

Understanding lithium-ion transport in tunnel-structured manganese oxides is essential for designing high-performance lithium-ion battery electrode materials. Here, we elucidate the early-stage lithiation mechanism of potassium-stabilized α-MnO 2 nanowires using in situ transmission electron microscopy (TEM) coupled with electron energy-loss spectroscopy (EELS), high-resolution TEM (HRTEM), and geometric phase analysis (GPA). Real-time TEM imaging reveals clear volume expansion at the reaction front, while EELS analysis uncovers lithium-ion diffusion far beyond this region, where no visible expansion is observed, indicating fast, defect-assisted transport. GPA and HRTEM analyses show that localized tensile and compressive strain fields, originating from pre-existing local tunnel structural variations, persist after lithiation. The tensile-strained regions enable lithium-ion insertion with minimal lattice distortion, offering additional free volume that facilitates rapid lithium-ion accommodation ahead of the structural transformation. Our results demonstrate a local tunnel variation-mediated fast diffusion pathway that precedes bulk reaction, underscoring the critical role of local strain in enabling early-stage lithium transport. Given the structural versatility of MnO 2 and its ability to accommodate diverse atomic arrangements beyond the well-known tunnel phases (β-, γ-, δ-, λ-, R-phases), our findings highlight the importance of understanding and engineering local structural environments. This work provides fundamental insights into the interplay between defects, strain, and ion dynamics, and presents defect engineering as a promising approach to enhance both rate performance and structural stability in manganese-based cathodes.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND