Strategies for Fabricating Molybdenum Structures Using Laser Powder Bed Fusion

Abstract

Advances in manufacturing techniques are viewed as enabling technologies for development of high performance nuclear fuel forms that couple high uranium density with improvements to key properties such as thermal conductivity unattainable through conventional fabrication routes. Additive manufacturing (AM) enables the fabrication of complex fuel geometries that are difficult or impossible to achieve using conventional manufacturing methods. Melting-based AM processes, such as laser powder bed fusion (LPBF), provide high geometric resolution (>200 µm depending on the feature) across a variety of metal alloys, including those suitable for high-temperature fuel cladding applications, such as Nb, W, and Mo. Molybdenum is particularly attractive due to its high thermal conductivity, low thermal expansion, and excellent mechanical stability at elevated temperatures. However, its high melting temperature and brittle nature at low temperatures pose significant challenges during LPBF processing. Rapid solidification inherent to LPBF induces high residual stresses, often leading to post-solidification cracking, which limits the manufacturability of Mo components via this method.