Thermoelectric Behavior of Structurally Disordered Lanthanide and Actinide Silicides

Abstract

Lanthanide and actinide intermetallic materials exhibit intriguing electronic, structural, and magnetic properties arising from their partially filled f orbitals. Strong f-electron correlations can significantly modify the electronic density of states, carrier scattering, and transport behavior, making these systems promising candidates for unconventional thermoelectric materials. In previous studies, single crystals of A1.33T4Al8Si2 (A = Ce, Th, U, Np; T = Co, Ni) were synthesized. This structure consists of ordered TAl2 corrugated double layers separated by disordered An–Si monolayers. The inherent disorder within the An–Si layers has been linked to unusual magnetic behavior, such as spin-glass phenomena, and is expected to strongly influence phonon scattering and charge-carrier transport relevant to thermoelectric performance. However, the thermoelectric properties of this material family have not previously been explored. In this work, DFT calculations were performed to evaluate the electronic density of states, band structures, and thermoelectric properties, including the effects of doping. To validate these predictions, Ce1.33Co4Al8Si2 single crystals were grown and experimentally characterized. Additionally, a new Yb1.33Co4Al8Si2 phase was synthesized and characterized using single-crystal XRD, SEM-EDS, magnetization measurements, and thermoelectric measurements. These results provide insight into structure–property relationships governing thermoelectric behavior in f-electron intermetallics and offer guidance for future thermoelectric materials.