Modeling Marangoni Convection using a Velocity-Time Relationship

Abstract

The Waste Treatment and Immobilization Plant (WTP) at the U.S. Department of Energy’s (DOE’s) Handford site is designed to treat 56 million gallons of radioactive waste through vitrification. The melting vessels physical and chemical integrity is essential to maintain, as failure has a high safety and financial penalty. Monofrax® K-3 refractory, the material widely used for the melting vessel, undergoes significant corrosion over time, concentrated at the triple-point junction between the gaseous atmosphere, refractory, and glass melt, producing a characteristic neck-like profile that significantly limits refractory service life. Accurate prediction of the corrosion within the melter can be used to prevent this and extend the lifetime of the melters. A computational fluid dynamics (CFD) model was previously developed, and predicted subsurface refractory corrosion, but failed to predict the neck-line profile observed experimentally. To address this limitation, the glass-melt meniscus geometry at the glass-refractory interface was estimated from experimentally measured neck profiles and wettability experiments. A curve was fitted to the neck profile to identify the triple point location, and the meniscus shape was characterized by a contact angle of 1°. A velocity profile accounting for Marangoni convection-driven corrosion was derived from the estimated meniscus geometry. Surface tension measurements from LORPM14R1 glasses of varying composition were coupled with K-3 coupon dissolution rates to establish a surface tension–time relationship. This analytical velocity-time model was integrated into the existing CFD framework to improve prediction of the neck corrosion profile. Work was done in a computational setting with national collaboration, resulting in professional development through presentational and technical writing growth.