Sintering effects on NpO 2 grain size and morphology: The role of precursor Np phase

Abstract

Neptunium dioxide (NpO 2 ) is a key phase in nuclear material processing as a target material for the production of plutonium-238 ( 238 Pu) and has been historically synthesized via the calcination of a Np oxalate precursor. Alternative synthesis methods for NpO 2 are now more prevalent, necessitating their study and comparison with the more common oxalate route. The purpose of this work was to investigate the microstructural properties of NpO 2 synthesized from a nitrate-based Np precursor phase via the assessment of NpO 2 particle size and morphology as a function of calcination temperature and time. Scanning electron microscopy (SEM) was used to probe the primary grain size and morphology of NpO 2 after calcination at temperatures ranging from 700 to 1100 °C and hold times ranging from 1 to 10 h. Post-image analysis using ImageJ software enabled the quantification of mean particle diameter. This analysis indicated that particle diameter increases with both increasing calcination temperature and hold time. Primary particles were shown to be clumped in irregular patterns into the overall rough, blocky aggregates, but this macroscopic morphology was not affected by calcination time or temperature. Although trends in primary grain size of NpO 2 were consistent with available literature from other Np precursor phases, the macroscopic morphology of the NpO 2 aggregates was quite different than reported for other precursors. Through comparison with historical literature on Np oxalate, this work emphasizes the importance of Np precursor on the physical properties of NpO 2 .