Computational thermodynamics-guided alloy design and phase stability in CoCrFeMnNi-based medium-and high-entropy alloys: An experimental-theoretical study

Abstract

A computational thermodynamics approach has been employed to design CoCrFeMnNi-based medium- and high-entropy alloys (M/HEAs) with systematically varied compositions (Co(( 80-X )/ 2 )Cr(( 80-X )/ 2 )Fe X Mn 10 Ni 10 with x = 30, 40, and 50 at.%) and phase stability. Since the formation of sigma phase, usually brittle and undesirable, is a common concern, when this class of alloys is subjected to elevated temperatures (600–1000 °C), predicting its formation becomes essential. Thus, its formation and the phase equilibria were studied using the CALPHAD method, and two empirical methods, namely, valence electron concentration (VEC) and paired sigma-forming element (PSFE). Isothermal aging treatments at 900–1100 °C for 20 h were performed, since CALPHAD and VEC/PSFE predictions diverged. Both prediction methods were compared with experimental characterization by a combination of scanning electron microscopy and high-energy synchrotron X-ray diffraction. In conclusion, the predictions from the VEC/PSFE and CALPHAD calculations (depending on the database used) were shown to be quite accurate.