Development of thermal joints for conduction-cooling applications

Abstract

Abstract In support of the development of conduction-cooled superconducting radiofrequency (SRF) niobium cavities for use in continuous-wave linear accelerators, an experimental study of thermal contact resistance was performed on bolted joints using high-purity niobium, aluminium, and copper along with Apiezon N grease and indium foil as interfacial materials. The geometry of each joint investigated aims at replicating the design adopted in conduction-cooled SRF cavities currently under development at Jefferson Lab. The materials’ thermal conductivity and the joints’ thermal resistance were measured in the temperature range of 3.5 - 10 K. The results showed that the low thermal contact resistance of 2-4 K·cm 2 /W at 4.3 K achieved with Al-In-Nb and Al-Apiezon N-Cu joints should allow the operation of conduction-cooled SRF cavities at a targeted accelerating gradient of ∼10 MV/m.