Henry’s Solubility and Diffusion Coefficients for 29 Volatile Organic Compounds in Polydimethylsiloxane Sylgard 184 at 293 K

Abstract

Two-dimensional (2D) inverse gas chromatography (IGC) enables simultaneous determination of Henry’s solubility and Fickian diffusion coefficients for volatile organic compounds (VOCs) in polymer films. This technique offers a significant advantage over traditional cylindrical column IGC by providing precise control and measurement of the film thickness (here, 0.064 ± 0.002 mm), which is the critical length scale for accurate diffusivity determination. We apply this methodology to characterize VOC transport in Sylgard 184, a widely used polydimethylsiloxane (PDMS)-based polymer containing substantial silica filler content. At room temperature (20 °C), we measured solubility and diffusion coefficients for 29 common VOCs spanning diverse chemical functionalities, including alkanes, aromatics, chlorinated solvents, ketones, esters, and alcohols. Comparison with literature data for pure PDMS reveals that VOC solubility in Sylgard 184 is generally higher; for most non-hydrogen-bonding compounds it remains within a factor of 2 of pure PDMS, whereas alcohols are enhanced by roughly 1.8 to 3.7 times, which we attribute to favorable interactions with residual silanol groups on the silanized silica filler. Diffusion coefficients range from 1.0 × 10 –6 cm 2 /s (n-undecane) to 8.9 × 10–5 cm 2 /s (acetonitrile) and align well with extrapolated literature values for PDMS. This study provides essential thermodynamic and transport data for predicting VOC permeation in Sylgard 184 while demonstrating the utility of 2D IGC as a robust technique for characterizing rubbery polymer membranes across diverse industrial applications.