Integrated Simulation of Weld Residual Stress Evolution and Crack Propagation Using XFEM

Abstract

Nuclear power plant components operate in environments that promote multiple degradation mecha- nisms, several of which involve crack initiation and growth. An ongoing effort in the U.S. Department of Energy’s Nuclear Energy Advanced Modeling and Simulation (NEAMS) program is developing a general capability within the Multiphysics Object Oriented Simulation Environment (MOOSE) framework for simulating three-dimensional crack growth under a range of driving conditions, including fatigue, stress corrosion cracking (SCC), brittle fracture, and stress-relaxation cracking. This report demonstrates an end-to-end workflow that uses this capability to model weld-residual-stress-driven SCC in the J-groove weld of a pressurized-water reactor control rod drive mechanism penetration in the vessel head. The workflow consists of a thermomechanical welding simulation with temperature-dependent plasticity, followed by cooldown to ambient conditions, and a restart of the simulation using the MOOSE extended finite element method (XFEM) module to propagate a three-dimensional crack through the residual stress field. New welding capabilities were developed to properly initialize newly activated elements in the weld region, and robustness improvements were made to the mesh-based algorithm for defining cutting planes in the 3D XFEM algorithm, allowing it to handle complex crack fronts and stress fields. Together these advances allowed the simulated SCC crack to grow from an initial elliptical flaw in the weld, across the weld, through the tube wall, and almost to the triple point (where the weld, tube, and reactor pressure vessel head intersect) over roughly 36 years of simulated service. These results demonstrate a workflow that can be extended to fully three-dimensional welding simulations and more complex crack interaction problems.