Computational simulation of asymmetric phase transformation in cracked Li₇La₃Zr₂O₁₂: Variant selection and chemo-mechanical implications

Abstract

Coupling between microcracks and phase transformation in ion-conducting ceramics can jointly affect mechanical responses and ion transport. In this work we investigate the cubic-to-tetragonal phase transformation in Li₇La₃Zr₂O₁₂ in the presence of a microcrack under hydrostatic loading and quantify its implications for crack-tip stress concentration and Li-ion transport using phase-field and molecular dynamics simulations. The phase transformation exhibits a strong asymmetry between hydrostatic tension and compression. Under tension, the crack edge nucleates one tetragonal variant that amplifies the crack-tip stress intensity and promotes crack opening. Under compression, the crack tip nucleates a different tetragonal variant that enhances the stress-induced crack-closure tendency. Effective Li diffusivity analysis shows faster transport degradation under compression due to accelerated transformation kinetics, exposing a trade-off between mechanical stability and ionic conductivity. These results highlight the intertwined nature of cracking, phase transformation, and ionic transport in ion-conducting oxides and provide mechanistic insights into chemo-mechanical degradation of solid electrolytes.

Explore related subjects

Keep this discovery

BibTeXRIS

Feng, Longsheng [Wayne State Univ., Detroit, MI (United States); Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF)] (ORCID:0000000308453656), Wang, Bo [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF); Pennsylvania State Univ., University Park, PA (United States)] (ORCID:0000000331465559), Yuan, Suyue [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF)], Kim, Kwangnam [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF)], Wood, Brandon C. [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF)], Wan, Liwen F. [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF)] (ORCID:0000000253910804), Heo, Tae Wook [Lawrence Livermore National Laboratory (LLNL), Livermore, CA (United States). Laboratory for Energy Applications for the Future (LEAF)]. 2026-10-01. Computational simulation of asymmetric phase transformation in cracked Li₇La₃Zr₂O₁₂: Variant selection and chemo-mechanical implications. https://doi.org/10.1016/j.scriptamat.2026.117438

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

Improving Ionic Conformality Across Polymer Electrolyte|Electrode Interfaces

Maintaining uniform ionic transport at electrode|electrolyte interfaces, i.e., ionic conformality, remains challenging in polymer electrolyte (PE)-based solid-state batteries. Morphological conformality does not necessarily imply ionic conformality. In PEs, which typically consist of a mechanically supporting component and distinct ionically conductive components, the rearrangement or depletion of mobile ion-conductive domains at interfaces can disrupt ionic transport pathways. Such localized ionic depletion contributes to interfacial instability and capacity degradation in high-voltage lithium-metal batteries. Herein, an electrolyte design approach aimed at minimizing interfacial heterogeneities is demonstrated through compositional adjustments, characterized by spatially resolved structural and chemical X-ray techniques and NMR diffusometry to elucidate ion transport dynamics. This approach improves ionic conformality at electrode interfaces, enhancing cycling stability in Li||LiNi 0.8 Co 0.1 Mn 0.1 O 2 (NMC811) coin and pouch cells cycled at high voltages. These results contribute to understanding interfacial behaviors in multiphase PEs and inform strategies for improving stability across solid-state battery interfaces.

36 MATERIALS SCIENCE

Evaluating Fracture Behavior of Bioinspired Alumina-YSZ Composites through Static and Dynamic Mechanical Testing

Ceramic materials are known for their high hardness and strength but are limited by low toughness and sudden failure. Inspired by the microstructure of dental enamel, which features undulating rods that promote crack deflection and energy absorption, architected specimens were designed and manufactured. A bespoke ball-on-ring (BoR) testing apparatus measured the static biaxial rupture strength of these bioinspired materials. Additionally, impact testing with spherical steel projectiles assessed their behavior under dynamic conditions. Monolithic alumina specimens were compared to architected alumina reinforced with yttria-stabilized zirconia (YSZ) rods produced via direct ink write 3D printing. BoR tests revealed that monolithic alumina had a Weibull modulus of 10.53 and a characteristic strength of 372.3 MPa, while the composite specimens showed a Weibull modulus of 5.46 and a characteristic strength of 213.3 MPa. Although the composite failed at lower stresses and projectile velocities, it exhibited notable crack deflection and fracture resistance, with cracks being effectively interrupted by the rod inclusions. The composite specimens also resulted in fewer and larger fragments upon impact. Finite element simulations confirmed the effectiveness of the rod structures in enhancing fracture resistance.

Bioinspired materials