Studying Perovskite Solar Cells in Reverse Bias to Accelerate and Investigate Degradation Due to Electrochemistry and Halogen Migration

McGehee, Michael D [University of Colorado] (ORCID:0000000196099030)
View original source ↗Read source document ↗Export metadata ↓

Abstract

This project improved the understanding of how electrochemical reactions cause degradation when perovskite solar cells are operated in reversed bias. Atomic layer deposition of

Explore related subjects

14 SOLAR ENERGYPerovskite Solar Cell

Keep this discovery

BibTeXRIS

McGehee, Michael D [University of Colorado] (ORCID:0000000196099030). 2026-05-11. Studying Perovskite Solar Cells in Reverse Bias to Accelerate and Investigate Degradation Due to Electrochemistry and Halogen Migration. https://doi.org/10.2172/3408470

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

14 SOLAR ENERGY subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

DOE OSTI2026

Semi-Transparent Perovskite Solar Cells in a Stacked Tandem Module: Cooperative Research and Development Final Report, CRADA Number CRD-19-00810

This project seeks to develop device design, materials composition, and processing tools and parameters to fabricate semi-transparent perovskite solar cells and modules for application in stand-alone products or added to other solar cells in a mechanically stacked tandem configuration. This technology presents significant advanced manufacturing challenges and opportunities in getting to scale, including development of perovskite inks, scalable perovskite and heterojunction deposition and annealing processes, heterojunction composition, transparent electrode composition and deposition process, anti-reflection layer composition and deposition process, and cell to module integration processes. Modification 5: The proposed project seeks to develop device design, materials composition, and processing tools and parameters to fabricate semi-transparent perovskite solar cells and modules for application in stand-alone products or added to other solar cells in a mechanically-stacked tandem configuration. This technology presents significant advanced manufacturing challenges and opportunities in getting to scale, including development of perovskite inks, scalable perovskite and heterojunction deposition and annealing processes, heterojunction composition, transparent electrode composition and deposition process, passivation layers including in module scribes, anti-reflection layer composition and deposition process, and cell to module integration processes. Advanced metrology and characterization will be performed on perovskite films, cells and module. Furthermore, we will examine module or materials recycling for circular economy considerations. Modifcation 6: Gigahertz frequency microwave pump-probe spectroscopies are highly sensitive to thin film semiconductor photoconductivity of individual and stacks of layers that comprise perovskite solar cells. As such, these techniques will be used to qualify reproducibility and quality correlations during the manufacturing process. Modification 7: Mechanical adhesion of top contacts within perovskite modules significantly impacts the durability of the module when exposed to accelerated degradation testing. The adhesion between the perovskite/transport layer interface and the transport layer/top contact interface are both very sensitive small changes in processing. ALD processing conditions of the transport layer will be tuned to optimize the mechanical adhesion within the perovskite module stack.

14 SOLAR ENERGY↗
DOE OSTI2026

Research and Development Related to the Commercialization of Perovskite Radiation Detectors (CRADA Final Report)

This work will focus on the development of perovskite radiation detectors fabricated with nanocrystal, thick polycrystalline films, or single crystal materials. This will harness NREL’s instrumentation and expertise in a variety of research areas including but not limited to metal halide perovskites, device characterization, device packaging, accelerated lifetime testing, and ink chemistry development.

14 SOLAR ENERGY↗
NASA NTRSDate not supplied

Quantifying Primary Arc-Induced Degradation of Perovskite Solar Cells

Primary arcing induced by spacecraft charging presents a significant hazard to thin film solar cells if left unchecked. Here, we present the results of a preliminary effort to quantify the impacts of primary arcing to perovskite solar cells. Solar cells operating in a charged environment are susceptible to electrostatic discharges known as arcing. While primary arcs are not generally considered a major concern for traditional space PV, for thin film cells, these can induce significant heating and subsequent damage. We conducted ESD testing in a LEO-like plasma in the National Plasma Interaction Facility at NASA Glenn Research Center to quantify impacts to cell performance by arcing. The perovskites tested saw a decrease of short circuit current with an increased number of arcs, averaging a relative change of 73.89 ± 15.90% after 60 total arcs supplied a cumulative energy dose of 76.12 mJ to the string. Ongoing work entails testing with larger perovskite data sets and expanding to include additional thin film cell technologies to demonstrate the risk unmitigated primary arcing presents.

primary arcing↗