DOE OSTI · 3411903
PowerPoint Slides for Materials Characterization and Testing support
Explore connections, maps & timelines
Demma, Anne Genevieve [Idaho National Laboratory]. 2026-05-06. Materials Characterization and Testing support. https://www.osti.gov/biblio/3411903
Cite the original work for its findings. Save a collection to share your selection of sources.
KEEP EXPLORING
Three-dimensional (3D) focused ion beam (FIB) tomography enables reconstruction of internal nuclear fuel features that can't be fully evaluated through surface imaging alone. This capability supports characterization of fuel constituents and defects under thermal and irradiation conditions relevant to microreactor development. However, large tomography datasets can create data-handling, loading, and visualization challenges, especially when image-stack preparation and file conversion must be completed with separate tools. The Computational Ultraspatial Tomography Toolkit for High-Resolution Object Analysis Tools (CUTTRHOAT) is an open-source web application being developed to display FIB tomography datasets available through the Nuclear Research Data System (NRDS). The current alpha version requires prepared HDF5 datasets and has limited integrated data-preparation capabilities. This project improves CUTTHROAT by adding dataset-folder selection, automatic input detection, dataset scanning, missing-slice identification, blank-slice insertion, and image-stack-to-HDF5 conversion. Two applications will be compared: the baseline CUTTHROAT alpha workflow and the updated application containing the integrated data-handling and preprocessing functions. Evaluation will consider dataset detection accuracy, conversion success, loading time, rendering responsiveness, application stability, and user interaction. Preliminary results demonstrate successful loading of existing HDF5 files and converted image stacks, while testing also identified performance reductions caused by excessive blank-slice generation. The updated workflow reduces reliance on external preparation tools and supports more direct movement from image stacks to color-code 3D visualization. Future work includes refining missing-slice handling, integrating additional preprocessing functions, like a denoising feature, parsing TIFF metadata for automatic voxel scaling, and adding manual X, Y, and Z voxel-spacing inputs for PNG and JPEG.
Generation IV nuclear reactors require structural materials capable of withstanding high temperatures, corrosion, and radiation damage. Refractory high entropy alloys (RHEAs) show potential due to their resistance to irradiation damage, reduced void swelling, and microstructural stability. However, most previous studies have focused on thin films and ion irradiation, leaving the neutron irradiation response of bulk RHEAs largely unexplored. Mechanical behavior results show brittle behavior before and after irradiation. The addition of Zr led to an increase in hardness due to Zr-rich precipitates in the bulk microstructure. Lastly, hardness results showed an increase in hardening after irradiation indicating irradiation induced hardening has occurred.
Silicon carbide has been identified as a useful material for nuclear application due to its heat resistance, low neutron absorbing cross-section, chemical inertness, and its rigidity as a structural material. These properties make it very favorable for high temperature environments such as in TRISO fuel and advanced reactor designs. Treatments such as n-doping, where carrier atoms are added to increase the number of free electrons, are expected to further improve properties such as thermal conductivity and electrical resistivity. Due to the high amount of neutron interactions in a nuclear reactor, it is expected that silicon carbide used in a reactor will be passively n-doped via transmutation. Studying the effects of n-doping in silicon carbide can help us better understand how the material will operate under real world conditions. We have found that n-doping the SiC increases both thermal and electrical conductivity, providing positive feedback under reactor usage. Previously it had been thought that under reactor conditions material properties of SiC could only degrade due to defects caused by neutron interactions. This study shows that transmutation doping can help to counteract and slow this process. This research shows that SiC can be used in nuclear reactor components contrasting with more costly and complicated alternative materials.