ELASTOMERIC MICROVASCULAR SELF-HEALING MATERIALS

Abstract

Damaged elastomeric diaphragms within pneumatic controllers used in the oil and gas industry lead to an unintended release of methane. Self-healing microvascular materials capable of healing various types of damage have been fabricated. These microvascular materials are designed to replace currently available commercial diaphragms found in pneumatic controllers and provide a solution to reduce unintended methane leaks. Poly(dimethylsiloxane) (PDMS) was used as the main matrix material, with additional testing conducted on polyurethane and flexibilised epoxy materials. Microvascular networks were implemented into the elastomeric membranes to act as ves- sels to deliver healing agents to the damaged areas. The complex, interdigitated channel networks were created using a 3D printed custom compounded filament composed of polylactic acid (PLA) and tin(II) oxalate. Two-part liquid casting polymers were poured around the channels into a mould to create samples with the scaffolding of the microvascular channels intact. Hollow microvascular networks were created by placing the samples within a vacuum oven at 250◦C which causes the thermal depolymerisation of PLA into its gaseous monomers. The manufactured materials were placed in test stands and pressurized using nitrogen gas to determine their healing and mechanical behaviour. Self-healing behaviour was demonstrated using PDMS matrix materials and healing chemistries within a pressure test cell. This test cell was designed to detect any damage to a sample by record- ing an outlet pressure. Damages including puncture holes, diagonal cuts and star-shaped central iv cuts were applied to the samples and a reduction in the outlet pressure was recorded for all sam- ples. A variation in channel spacing and diameter was studied to determine the optimal design of the microvascular network for self-healing performance. The mechanical performance of elastomeric membrane materials within a diaphragmatic pressurised stand was observed. Deformations and strains around the channels and channel inter- sections at the midplane of the materials were recorded using digital image correlation. Normal stresses were calculated using Hooke’s law and the material properties of the PDMS matrix. A reduction in leak rate, implying the success of self-healing, was recorded within manu- factured diaphragm samples tested within a commercial valve. PDMS is the favourable material when compared to polyurethane and flexibilised epoxy for creating