Engineering Microstructure in Dry-Processed Cathodes Via Calendering

Abstract

Calendering serves as a multifunctional step in dry electrode processing that not only densifies the electrode but also induces polytetrafluoroethylene (PTFE) fibrillation and reorganizes the microstructure. These coupled effects are essential for achieving electrical connectivity and sufficient cohesion, yet they also introduce trade-offs, such as active material particle fracture, pore collapse, and excessive porosity loss, that can hinder ionic transport. This research systematically maps the calendering parameter space for LiNi0.6Mn0.2Co0.2O2 (NMC622) dry cathodes with a target thickness of ∼100 µm and porosity of ∼30% by varying roll gaps, roll temperature, roll speed, and the number of passes. A practical processing window for this formulation and electrode architecture is identified that achieves sufficient PTFE fibrillation and strong interfacial contact while minimizing particle fracture and preserving the porosity required for efficient ionic transport. In particular, gradual-gap calendering with moderate per-pass compression mitigates fracture and pore collapse while still reaching the target thickness with reasonable throughput, and slower roll speeds with modest roll temperatures further reduce mechanical damage. These results provide actionable guidance for scaling NMC622-based thick dry-processed cathodes.