Characterization of lateral amorphous selenium photodetectors for low-photon and VUV detection at cryogenic temperatures

Abstract

The performance of amorphous selenium (a-Se) as a cryogenic photodetector material is evaluated through a series of experiments using laterally structured devices operated in a custom optical test stand. These studies investigate the response of a-Se detectors to low-photon fluxes at high electric fields near avalanche conditions, the linearity of the photoconductive response over a wide dynamic range and the direct detection of narrowband 130 nm vacuum ultraviolet (VUV) illumination. At 87 K, matched-filter analysis shows reliable single-shot detection with efficiencies ≥80% and area under the curve (AUC) ≥ 0.85 using as few as ∼ 6800 incident 401 nm photons, corresponding to ∼ 3400 photons within field-active regions after accounting for geometric constraints. Measurements are performed at cryogenic temperatures using calibrated photon fluxes derived from a silicon photomultiplier reference and a characterized optical filter stack. Additional experiments using a tellurium-doped a-Se (a-SeTe) device explore the material's behavior under identical test conditions and demonstrate that avalanche is achievable in a-SeTe at cryogenic temperatures. The results demonstrate reproducible low-noise operation, VUV sensitivity and field-dependent gain behavior in a lateral a-Se architecture, representing the first reported observation of avalanche multiplication in laterally structured a-Se and a-SeTe devices at cryogenic temperatures. These findings support the potential integration of laterally structured a-Se devices into next-generation pixelated liquid-argon time projection chambers (TPCs) requiring scalable, high-field-compatible photon detection systems.