Compatibility of Type 304H Stainless Steel in Static Molten FLiBe for Inertial Confinement Fusion Reactors: Role of Impurities and Redox Control

Abstract

Molten fluoride salts, such as FLiBe (LiF-BeF2), are promising candidates for tritium breeding and heat transfer in fusion reactors, but corrosion of structural materials remains a major challenge. This study investigates the corrosion behavior of austenitic stainless steel 304H in purified and NiF2-containing FLiBe at 500°C and 600°C, focusing on the effects of impurities and redox control. Exposure to purified FLiBe resulted in the concurrent depletion of Cr, Mn, and Fe, with corrosion at 500 °C dominated by the combined oxide formation and elemental dissolution, while at 600°C elemental depletion was predominant. The addition of a controlled NiF2 impurity significantly accelerated corrosion at both temperatures, demonstrating the sensitivity of 304H to the salt redox state. Beryllium additions were effective in mitigating corrosion for both baseline and NiF2-containing FLiBe; minimal depletion of Cr, Mn, and Fe occurred with Be additions as low as 2.5 mg (147 wppm), and no NiBe intermetallics formed at 5 mg (294 wppm), indicating that small Be inventories can provide substantial protection without deleterious phase formation. Thermodynamic equilibrium and coupled thermodynamic-kinetic analyses at the salt-alloy interface suggested low corrosion rates in systems with limited hydrogen fluoride (HF) generation, highlighting the importance of salt redox control. Estimates for a Be addition rate were calculated for the HYLIFE-II fusion reactor that can mitigate corrosion-induced degradation, assuming complete conversion of tritium to tritium fluoride (TF). Overall, 304H shows reasonable compatibility with FLiBe under optimized redox conditions. These results provide quantitative guidance for material selection and salt management in fusion blanket and heat exchanger systems and motivate validation under flowing, nonisothermal, and irradiated conditions.

Keep this discovery

BibTeXRIS

Pillai, Rishi [ORNL] (ORCID:0000000243688197), Sur, Deb [ORNL] (ORCID:0000000279549949), Cambier, Severine [ORNL] (ORCID:0009000209157293), Willoughby, Adam [ORNL], Lowe, Tracie [ORNL], Zhao, Youyang [Xcimer Energy], Bye, Amanda [Xcimer Energy], Reyes, Susana [Xcimer Energy]. 2026-08-01. Compatibility of Type 304H Stainless Steel in Static Molten FLiBe for Inertial Confinement Fusion Reactors: Role of Impurities and Redox Control. https://doi.org/10.1080/15361055.2026.2700693

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Compositional Homogeneity in Rapidly Solidified 316L stainless steel produced by laser powder-bed fusion processing

The segregation of alloying elements in rapidly solidified 316L stainless steel produced using additive manufacturing technologies is widely reported throughout literature. The microstructure of thin walls manufactured from 316L stainless steel using laser powder bed fusion are examined for the presence of alloy segregation, i.e. the rejection of solutes to grain boundaries. Metallographic methods including mechanical polishing and chemical etching are used to prepare samples for microanalysis m

Jankowski, Alan F. [Sandia National Laboratories (

Reduced instability growth and improved radiation trapping with optimized shock timing in double-shell inertial confinement fusion capsules

The double shell is a volume-burn inertial confinement fusion concept consisting of two concentric shells: a low-Z outer shell that collides with and transfers momentum to a high-Z inner shell which compresses and heats the thermonuclear fuel. The increased number of capsule interfaces and severe hydrodynamic instability of the high-density pusher during its acceleration phase provide challenges to the success of the double shell. Two-dimensional radiation-hydrodynamics simulations predict the hydrodynamic instability growth on the outer surface of the pusher can be greatly reduced through appropriate timing of two shocks that cross this interface. One of these shocks, unique to multi-shell designs, arises from radiation-driven ablation of the inner shell ahead of the main shock, the second shock of concern. The shock timing is optimized by increasing the thickness of a low-Z tamper layer exterior to the pusher, resulting in only minimal changes to the implosion timing. Reducing the instability growth on the outer surface of the high-Z pusher can dramatically decrease the modulations that feedthrough to the pusher inner surface, improving the efficacy of radiation trapping in the thermonuclear fuel and increasing the predicted thermonuclear yield by ≳20×.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY

Mercury Corrosion Loop Testing Program

The Mercury Corrosion Loop Testing Program continued through the second quarter. Materials to be tested in the 10 forced-convection test loops were selected; the materials are: Haynes 25, 9 Cr-1Mo alloy clad with Type 316 stainless steel, AM 350 stainless steel, and columbium (niobium) clad with Type 316 stainless steel. The eight-test-cell facility was completed and all utilities were installed. Pneumatic and electronic instrumentation for all test cells was installed and calibrated. Fabrication was initiated on the first four Haynes 25 loops. The first loop was 85% assembled at the end of the quarter. A centrifugal pump made from Type 316 stainless steel was tested; bearing modifications were made to improve operation.

Corrosion