Dielectric Spectroscopy Cable NDE for Unequal Aging Over Different Lengths

Abstract

This Pacific Northwest National Laboratory milestone report assesses the effect of unequal aging over different lengths of cable on dielectric spectroscopy (DS) bulk impedance measurements from the cable end. DS measurements can indicate the remaining useful life of cables; however, most benchmark tests are based on accelerated aging of the entire cable. If only a portion of the cable is exposed to a harsh environment (as is frequently the case), the DS measurement will indicate a significantly less-aged cable than if the entire cable were exposed to a uniform environmental stress. The DS measurement is primarily related to the intrinsic insulation material relative permittivity—typically between 1.5 and 3.0. Insulation aging increases permittivity and, correspondingly, the cable’s overall capacitance measured from the cable end. To judge the health of the overall cable system, operators are primarily interested in the condition of the most severely aged section since that is where a failure is most likely to occur. This can be expressed as the dimensionless relative permittivity of the severely aged section divided by the permittivity of a pristine cable. This relative permittivity is an intrinsic material parameter independent of cable length and can serve as a quantitative indication of the insulation condition. If the relative percentages of cable exposed to a harsh and benign environment are known, the DS measurement of the entire cable length, including both pristine and aged sections, can be compensated to predict the relative permittivity (relative to pristine permittivity) of the most severly aged segment. A test was performed on three 50 ft (16 m) cables with 10%, 50%, and 90% of the cable inside a thermal aging oven. Predictably, the aging effect on the DS response was greatest in the 90% sample, followed by the 50% sample, and then the 10% sample. The more interesting result is the ratio of the aged insulation permittivity to the pristine insulation permittivity. Based on prior work, an end-of-life cable has a value of approximately 1.35. If the relative percentages of pristine and severely aged cable lengths are known, and the total cable-length capacitance of the initial pristine cable and the combined pristine plus aged cable are known, the relative aged permittivity (ratio of aged section permittivity / pristine section permittivity) can be estimated. The relative cable lengths exposed to a harsh environment may be known or estimated based on plant layout drawings or cable reflectometry tests that can locate the oven entry and exit points. The compensation was verified using a lumped-parameter model to predict the aged-segment permittivity e2/e1, where e2 is the aged-segment permittivity and e1 is the pristine-segment permittivity. For all three percentages of aged cable lengths, the ratio was quite similar, as would be expected since all cable segments were exposed to the same aging environment. This ratio of aged permittivity to pristine permittivity can be compared to other damage indicating tests, including elongation at break, to assess cable condition.