Heterobimetallic Iridium-Niobia Catalyst for Efficient and Selective Methane Ammonia Reforming

Wu, Jiachun; Dubrawski, Zachary; Wu, Shiwen; Aissiou, Samy; Fang, Lingzhe; Veyre, Laurent; Thieuleux, Chloe; Li, Tao; Camp, Clement; Xiang, Yizhi

doi:10.1021/jacs.6c04917

DOE OSTI · 3701510

Heterobimetallic Iridium-Niobia Catalyst for Efficient and Selective Methane Ammonia Reforming

Wu, Jiachun·Dubrawski, Zachary·Wu, Shiwen·Aissiou, Samy·Fang, Lingzhe·Veyre, Laurent·Thieuleux, Chloe·Li, Tao·Camp, Clement·Xiang, Yizhi

View original source ↗Read source document ↗Export metadata ↓

Abstract

A Surface OrganoMetallic Chemistry (SOMC) approach, leveraging a molecularly defined heterobimetallic niobium–iridium complex, was used to prepare a mesoporous SBA-15 silica-supported Ir-NbOx catalyst. The resulting Ir-NbOx/SiO2 catalyst exhibited excellent catalytic performance in selective methane/ammonia reforming. Specifically, the Ir-NbOx/SiO2 catalyst showed significantly higher activity (turnover frequency 8.5 s–1), selectivity (75%), and stability than the Ir/SiO2 analog, whereas the NbOx/SiO2 counterpart was almost inactive. This contrasts with ethane/ammonia reforming via C–C cleavage, for which the bimetallic Ir-NbOx/SiO2 was less active than Ir/SiO2, demonstrating tuned selectivity toward C–H activation rather than C–C cleavage due to the Ir/NbOx synergy. Importantly, an Ir-NbOx/SiO2 reference catalyst, prepared by conventional impregnation/calcination/reduction steps, was found to be inactive, highlighting the value of the SOMC catalyst preparation approach using well-defined heterobimetallic precursors. These results represent a significant advance over existing catalysts due to the atomic-scale synergy between Ir and NbOx sites, enabling access to activity and selectivity regimes inaccessible to monometallic analogs.

Keep this discovery

BibTeX RIS

Wu, Jiachun, Dubrawski, Zachary, Wu, Shiwen, Aissiou, Samy, Fang, Lingzhe, Veyre, Laurent, Thieuleux, Chloe, Li, Tao, Camp, Clement, Xiang, Yizhi. 2026-07-15. Heterobimetallic Iridium-Niobia Catalyst for Efficient and Selective Methane Ammonia Reforming. https://doi.org/10.1021/jacs.6c04917

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Pivotal role of organic adsorbates for the creation of catalytic sites during dry reforming of methane

Inadvertent factors can sometimes be crucial for synthesis of catalysts. The use of polyalcohols is common in the synthesis of heterogeneous catalysts. Interactions between alcohols and heterogeneous catalysts have been shown to induce surface reconstructions that greatly impact catalytic performance. Thus, traces of these alcohol functionalities on the as-synthesized catalysts, combined with heat treatment, could be critical in the generation of catalytic sites. Here, we show that during the synthesis of a Ni–Mo/MgO catalyst using a polyol process, residual ethylene glycol (EG) on the surface plays a significant role in the generation of catalytic sites for dry reforming of methane (DRM). The as-synthesized catalyst presents dispersed cationic Ni. Under DRM reaction conditions, the presence of EG, and H2 generated in situ, promote the generation of co-localized Ni–Mo nanoparticles (NPs). Greater amount of EG in the as-synthesized catalyst prevented sintering, leading to better catalyst stability and higher rates. If the residual EG remaining post-synthesis is removed through calcination, before conducting DRM, NiO NPs are formed and the material is completely inactive for catalyzing the reaction. When using a different support, denoted MgO*, EG also proved indispensable to generate active sites, although Ni–Mo co-localization was not evident, and a combination of DRM-related species was needed to activate the catalyst, not just H2. This work systematically uncovers how the interactions between organic adsorbates, the supported metals and the catalyst support dictate the creation of catalytic active sites.

Polo Garzon, Felipe [ORNL] (ORCID:0000000265076183↗

DOE OSTI2025

AUTOIGNITION DELAY TIMES FOR REFORMATE GAS MIXTURES FROM METHANE GAS ENGINES

Methane slip is a prominent issue in natural gas reciprocating engines that are used in transportation and marine applications. The incomplete combustion that results in methane slip can be resolved with the introduction of hydrogen within the combustion mixture to improve methane oxidation and further enable combustion within the engine crevices where methane has previously remained unreacted. Steam methane reforming (SMR) is a common method used to produce hydrogen and can be used to design an onboard device to reduce methane slip from reciprocating engines. The development of this reformer device requires the validation of high-fidelity chemical kinetic models at the low temperatures of the crevice volumes of these engines. In this work, auto-ignition data is obtained using a shock tube at lean (φ—0.714 or λ—1.4) and stoichiometric (φ, λ = 1) equivalence ratios spanning a temperature range of 1042–1234 K at the 80-bar operating pressure of the test engine. Blends of methane, hydrogen, and reformate products from the SMR reaction are shock-heated in synthetic air, with the ignition delay time measured using an OH* chemiluminescence detector at 310 nm and a CH* detector at 430 nm. The experimental results are compared to several state-of-the-art chemical kinetic mechanisms from the literature. In general, most of the mechanisms show very good agreement with experiments at higher temperatures, with simulation results showing little deviation from experiments at lower temperatures. A sensitivity analysis was conducted, and the results reveal that the reaction H2 + CH3O2 = H + CH3O2H has a very significant role in determining low-temperature ignition delay times (IDTs) of SMR mixtures. These findings provide valuable insights into the chemical kinetics governing methane reformate combustion and contribute to the optimization of onboard reformer designs aimed at mitigating methane slip in natural gas-fueled engines.

Fraze, Matthew↗

DOE OSTI2026

Mitigating Hydrogen-Induced Degradation of Iridium Anodes in Proton Exchange Membrane Water Electrolyzers

One promising method for reducing precious metal usage in proton exchange membrane water electrolysis is lowering iridium (Ir) loading at the anode. However, low-loading Ir catalysts often suffer from poor stability under high current densities. In this study, hydrogen (H2) crossover from the cathode to the anode is identified as a key degradation pathway. Temperature-programmed reduction confirms the reduction of IrO2 at 80 °C in a hydrogen environment, highlighting the vulnerability of IrO2-based catalysts to H2 exposure. To mitigate this effect, palladium (Pd) is introduced as an anode additive, acting as an H2 oxidation catalyst and mitigating IrO2 reduction. This protective role is verified by inductively coupled plasma optical emission spectroscopy and in situ X-ray absorption spectroscopy, showing significantly suppressed Ir dissolution at 80 °C under H2 flow when an O-covered Pd surface is present at oxygen evolution reaction potentials. Results from the current study identify a new strategy in improving activity and durability of catalysts in electrolyzers.