Mechanistic Understanding of Interphase-driven Aging in Silicon Anodes

Abstract

Conventional solid electrolyte interphases (SEIs) strongly adhere to micro-silicon (µ-Si) and crack under volume changes, causing poor cycling performance. Nano-silicon improves cycling performance but remains costly with limited calendar life. Here potentiostatic ageing tests demonstrate that both calendar and cycle ageing are governed by SEI cracking and dissolution with different relative contributions. When the system is not dominated by SEI dissolution, the relative calendar life of Si anodes could correlates positively with their cycle life. LiF-rich SEI that enables long cycle life in µ-Si is therefore expected to enhance calendar life as well. Using this framework, we screened electrolytes, SEIs and electrodes and validated them with full-cell storage. LiF-rich SEI minimizes cracking and dissolution, enabling μ-Si to achieve excellent calendar life, whereas nano-silicon suffers from SEI dissolution and needs reduced electrolyte–electrode contact for better calendar life. This work clarifies calendar-ageing behaviour and accelerates electrolytes and SEI development for long-life Si anodes.

Keep this discovery

BibTeXRIS

Johnson, Christopher S.. 2026-02-03. Mechanistic Understanding of Interphase-driven Aging in Silicon Anodes. https://doi.org/10.1038/s41560-026-01967-1

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related discoveries

Unraveling interphase-driven failure pathways in LiMn0.6Fe0.4PO4/graphite pouch cells

LiMnxFe1−xPO4 (LMFP) is a promising high-voltage, thermally stable, and earth-abundant cathode material, yet its practical application is limited by interphase instability and Mn dissolution. In this work, we systematically evaluate LiMn0.6Fe0.4PO4/graphite pouch cells using three electrolyte formulations including control carbonate electrolyte, control + 2 wt% vinylene carbonate (VC), and control + 2 wt% VC + 1 wt% 1,3,2-dioxathiolane 2,2-dioxide (DTD), to establish how electrolyte composition governs interphase chemistry and long-term degradation. Electrochemical testing shows that both additives are preferentially reduced prior to ethylene carbonate (EC) during cell formation, generating robust cathode-electrolyte interphase (CEI) and solid-electrolyte interphase (SEI) layers that suppress gas evolution and raise the first-cycle coulombic efficiency to 89.3%. Additionally, the dual-additive electrolyte delivers the most stable performance, retaining over 85% capacity after 600 cycles while minimizing impedance growth under long-term cycling at C/3 and 40 °C. Soft X-ray absorption spectroscopy confirms that VC + DTD effectively suppresses electrolyte oxidation at the cathode surface, and micro-X-ray fluorescence shows substantially reduced Mn dissolution and deposition on the graphite anode. Density functional theory simulations further provided insights into the structural and energetic influences of alkoxide species on the cathode surface, proposing a Mn2+ extraction mechanism. The combined experimental and computational findings establish a mechanistic link between electrolyte composition and interphase evolution, highlighting the effectiveness of electrolyte engineering for extending the operational lifetime of LMFP-based lithium-ion batteries.

Chak, Chanmonirath Michael

Mechanistic origin of solvent-dependent thermal stability in sodiated Sn anodes for sodium-ion batteries

Understanding the thermal stability of high-energy density alloy anodes is critical for the safe deployment of sodium-ion batteries (SIBs). Here, accelerating rate calorimetry (ARC), post-mortem characterizations, and density functional theory (DFT) calculations are combined to understand the thermal reactivity of fully sodiated Sn, Sn-hard carbon (HC) blends, and HC anodes in carbonate- and ether-based electrolytes. ARC measurements show that propylene carbonate (PC) causes earlier self-heating rate (SHR) onset and higher reactivity than tetraethylene glycol dimethyl ether (TEGDME), indicating inferior thermal stability. Sodiated Sn exhibits better thermal stability than sodiated HC, while Sn-HC blends show intermediate behavior that improves with increasing Sn content. Post-ARC analyses reveal desodiation of Na15Sn4 to metallic Sn with particle coalescence, whereas Sn-HC blends and HC retain finer morphologies. PC promotes Sn oxidation to SnO, while TEGDME suppresses oxide formation; NaPF6-containing electrolytes additionally form NaF. DFT calculations show that PC adsorption lowers Na extraction energy and enhances interfacial electronic interactions, facilitating Na release and reductive decomposition. These results establish a direct correlation between solvent-dependent reaction pathways and thermal stability in SIB alloy anodes.

Accelerating rate calorimetry