Observation of N-rich solid-electrolyte interphase by ToF-SIMS.

Abstract

Formation of a stable solid electrolyte interphase (SEI) between lithium electrodes and electrolyte upon multiple charge/discharge cycles is crucial to a long-term lithium-ion battery performance. Addition of LiNO3 to lithium bis (fluorosulfonyl) imide/poly(ethylene oxide) (LiFSI/PEO) electrolyte leads to a durable SEI that is electrically insulating yet highly conductive to Li ions, chemically and electrochemically stable, physically uniform, and mechanically robust. ToF-SIMS was used here in combination with sputtering by a gaseous cluster ion beam (GCIB) to examine how the addition of a small proportion of LiNO3 to the LiFSI/PEO electrolyte affects the SEI composition. Negative ion ToF-SIMS spectra of the cycled samples display an intense m/z 26 peak associated with the SEI. Exact mass assignments and isotopic ratios indicate that this peak should be assigned as (CN-)-C-12, with little to no negative secondary ion signal arising from (LiF-)-Li-7. This CN- signal appears to arise from an N-rich portion of the SEI adjacent to the Li electrode that is depleted in LiF relative to the bulk electrolyte. The dearth of LiF- (and LiF+ from the positive ion spectra) is unexpected because LiF has been identified in the SEI in similar samples. Finally, GCIB sputtering indicates that the SEI adheres more strongly to the Li electrode than to the LiFSI/PEO electrolyte.