Novel PtNi single-atom–nanocluster (SA–NC) ensembles promote Tafel kinetics and ampere-class AEM hydrogen evolution

Abstract

The development of efficient, durable, and low-PGM electrocatalysts for the hydrogen evolution reaction (HER) in alkaline media is critical for next-generation electrolysis technologies. We report a facile two-step synthesis of highly dispersed PtNi and PtNi-nitride nanoclusters (NCs) (~2.3 nm) with ultralow Pt content (0.5 at.%) anchored on N-doped Vulcan carbon. Structural and compositional characterization via XAS, XPS, HAADF-STEM, HRTEM, and EDS mapping established key structure–activity relationships across varying Pt/Ni ratios and pyrolysis temperatures. The Pt0.5Ni0.5/C-750 catalyst, an ensemble of PtNi M-N-C type single-atom (SA) moieties with neighboring PtNi nanoclusters (NC), exhibited superior HER performance in alkaline media, achieving overpotentials of 30, 115, and 210 mV at 10, 100, and 500 mA cm−2, respectively. Despite at a lower Pt content, this novel SA–NC ensemble outperformed commercial Pt/C by ~36%. A standardized literature comparison with contemporary Pt- and Ru-doped analogues reveals the as-prepared Pt0.5Ni0.5/C-750 to sit at the apex of Tafel-limited kinetics and low overpotential at 100 mA cm−2. Tafel-limited Tafel slopes in both alkaline and acidic regimes confirm favorable proton recombination kinetics. Mass activities at 200 mV reached 13.8 and 18.84 A mgPt−1 in alkaline and acidic media, respectively. However, excessive nitridation (e.g., at 650 °C) adversely altered Pt electronic structure and HER kinetics. While Ni enhanced alkaline HER, acidic HER favored Ni-free analogues. Pt0.5Ni0.5/C-750 also demonstrated robust temperature responsiveness and 300-h operational stability at high current densities (0.5–1.0 A cm−2) in MEA tests. This work presents a scalable strategy for designing thermally responsive, durable, and compositionally tunable NC catalysts with neighboring SA moieties for alkaline electrolysis.