Draft ASME Code Case to qualify L-PBF 316H material for Section III, Division 5 applications

Abstract

This report documents the AMMT program’s development and submission of a draft ASME Code Case to qualify Laser Powder Bed Fusion (L PBF) Type 316H stainless steel for Section III, Divi-sion 5 Class A and SM high temperature nuclear applications. It summarizes the technical basis, the comprehensive high temperature mechanical test database assembled between 2023–2026, and the proposed code language and qualification framework submitted to ASME. The work was co-ordinated across multiple national laboratories and leverages prior ASME efforts to integrate additive manufacturing into the Boiler & Pressure Vessel Code. The body of the report describes the experimental database and analysis supporting the Code Case: tensile, creep, fatigue, creep fatigue, and thermal aging tests collected from multiple additive manufacturing sites, machine types, and powder lots, with material processed by a solution anneal heat treatment. The dataset — including both full size and subsized specimens and tests oriented parallel and perpendicular to build direction — shows limited tensile anisotropy, tensile properties comparable to wrought 316H, creep strength within the scatter of wrought material, but markedly reduced creep ductility above about 650 °C associated with rapid σ phase formation in L PBF microstructures. The draft Code Case itself prescribes a staged qualification model (manufacturing process qualification, component qualification, and per build witness testing), treats L PBF components as equivalent to Type 316 weld metal for design and inspection, and requires mechanical, chemical, and metallographic controls tied to ASTM/ISO 52946. Key acceptance criteria include tensile tests within a 90% prediction interval of the AMMT dataset, a creep fatigue screening test adapted from ASME Section III, Division 5, Subsection HB, HBB 2800 but with the cycle acceptance reduced to 100 for L PBF material, and double volumetric inspection of production components. The report concludes that the present data support treating L PBF 316H as analogous to conventional fusion weld metal for Division 5 design and inspection, while highlighting important caveats: the σ phase driven loss of creep ductility above ~650 °C, preliminary indications of enhanced creep fatigue sensitivity in some lots, and remaining gaps in long term aging and additional cyclic testing. Recommended next actions include completing outstanding cyclic and long duration creep/aging tests on the solution annealed condition, supporting inclusion of the 316H chemistry and heat treatment in ASTM/ISO 52946, and continuing engagement with ASME and NRC during balloting and review to enable industry adoption.