Monolayer Films of Binary Metal Oxide Nanoparticles for Carbon Nanotube Synthesis

Abstract

Binary metal oxide nanoparticles (biMO-NPs) combining transition and main-group metals with well-organized atomic architectures have unique potential as robust and economical heterogeneous catalysts. Herein, metal oxide nanoparticles (CoAlxOy) using cobalt and aluminum were synthesized, and their structure, morphology, and chemical composition were investigated using various characterization techniques. The biMO-NPs, which had a Gaussian-type size distribution (∼6 nm), were assembled on plain silicon substrates modified chemically with linker molecules bearing suitable end groups. Surface analysis revealed an ordered, uniform, close-packed arrangement of biMO-NPs forming a monolayer architecture with nanoscale thickness (∼12 nm), high surface uniformity, and negligible defects. The nanoparticle monolayer film (NP-MF) was employed as a catalyst to grow carbon nanotube (CNT) forests via the thermal chemical vapor deposition (CVD) method, similar to those grown from catalyst thin films deposited by physical vapor deposition. Structural characterization confirmed the growth of a dense, uniform, high-quality vertically aligned carbon nanotube (VA-CNT) forest with a length of ∼125 µm, which is comparable to the VA-CNTs grown from expensive thin films. Thus, CNT growth was successfully catalyzed by the biMO-NPs, highlighting a simple and inexpensive alternative for catalyst deposition. In this innovative wet-chemistry approach, the catalyst and catalyst support are combined within a single nanoparticle before NP-MF assembly. Interestingly, this approach provides a scalable and cost-effective pathway for CNT growth, eliminating the need for expensive thin deposition techniques.