Single-crystal NMC622 from combustion-assisted solid-state synthesis: Tunable particle size, voltage-dependent stability, and Li-ion diffusion

Abstract

Cost-effective and scalable synthesis of single-crystal lithium–metal-oxide cathodes with controlled size and morphology remains challenging for advancing high-performance lithium-ion batteries. Here, we demonstrate a solution combustion–assisted solid-state method for producing single-crystal NMC622 with tunable particle size at various lithium stoichiometries. Structural and electronic characteristics were probed using synchrotron-XANES, EXAFS, XRD and XPS, confirming well-defined coordination environments and phase purity up to Li ≈ 1.3. The electrochemical behavior of LixNMC (x = 1.0 and 1.3) single crystals was evaluated across 2.8–4.3 V and 2.8–4.7 V windows to elucidate the effects of lithium content and operating voltage. At 2.8–4.3V, Li1.3NMC exhibits higher initial capacity due to its larger lithium inventory, while Li1.0NMC shows superior long-term retention driven by its larger crystal size and reduced structural distortion. Increasing the cutoff voltage to 4.7 V enhances the initial capacity of both compositions by 17–25%, but long-term capacity retention ultimately converges to values comparable to those at 4.3 V due to voltage-induced degradation, where Li+ diffusion constant remains lying ranging from 10−12 –10−11 cm2s−1. Overall, this study establishes a scalable combustion-assisted route for synthesizing tunable single-crystal NMC622 and highlights the interplay between lithium stoichiometry, particle size, and voltage window in governing cathode stability.

Keep this discovery

BibTeXRIS

Roy, Subrata C [Jackson State University], Li, Mengya [ORNL] (ORCID:0000000295814044), Oketola, Oluwaseun [Jackson State University], Sahore, Ritu [ORNL] (ORCID:0000000223909570), Islam, Saiful M [Jackson State University]. 2026-05-01. Single-crystal NMC622 from combustion-assisted solid-state synthesis: Tunable particle size, voltage-dependent stability, and Li-ion diffusion. https://doi.org/10.1016/j.jpowsour.2026.240402

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

Chemical Bond Covalency in Superionic Halide Solid‐State Electrolytes

Abstract Halide solid‐state electrolytes (SSEs) are promising superionic conductors with high oxidative stability and ionic conductivity, making them attractive for all‐solid‐state lithium‐ion batteries. However, most studies have focused on ion‐stacking structures, overlooking the role of bond characteristics in ionic transport. Here, we investigate bond dynamics and the superionic transition (SIT) in bromide electrolyte, Li 3 InBr 6 , using synchrotron X‐ray techniques and ab initio molecular dynamics (AIMD) simulations. We demonstrate that the SIT in halide SSEs is driven by a thermally induced transition in bonding character (ionic to covalent) rather than a change in crystal phase. AIMD simulations further reveal enhanced Li⁺ diffusion and collective anion motion at elevated temperatures. Expanding our study to Li 3 LnBr 6 (Ln = Gd, Tb, Ho, Tm, and Lu), we confirm the widespread occurrence of SIT in this material class, with Li 3 GdBr 6 exhibiting the highest ionic conductivity (5.2 mS cm −1 at 298 K). More importantly, the ionic‐covalent transition is highly tunable through electrolyte modifications, such as cation/anion substitution and synthesis methods. Our findings provide a new perspective on ionic transport, highlighting the critical role of chemical bond characteristics in halide SSEs.

Chemistry

Eliminating chemo-mechanical degradation of lithium solid-state battery cathodes during >4.5 V cycling using amorphous Nb2O5 coatings

Abstract Lithium solid-state batteries offer improved safety and energy density. However, the limited stability of solid electrolytes (SEs), as well as irreversible structural and chemical changes in the cathode active material, can result in inferior electrochemical performance, particularly during high-voltage cycling (>4.3 V vs Li/Li + ). Therefore, new materials and strategies are needed to stabilize the cathode/SE interface and preserve the cathode material structure during high-voltage cycling. Here, we introduce a thin (~5 nm) conformal coating of amorphous Nb 2 O 5 on single-crystal LiNi 0.5 Mn 0.3 Co 0.2 O 2 cathode particles using rotary-bed atomic layer deposition (ALD). Full cells with Li 4 Ti 5 O 12 anodes and Nb 2 O 5 -coated cathodes demonstrate a higher initial Coulombic efficiency of 91.6% ± 0.5% compared to 82.2% ± 0.3% for the uncoated samples, along with improved rate capability (10x higher accessible capacity at 2C rate) and remarkable capacity retention during extended cycling (99.4% after 500 cycles at 4.7 V vs Li/Li + ). These improvements are associated with reduced cell polarization and interfacial impedance for the coated samples. Post-cycling electron microscopy analysis reveals that the Nb 2 O 5 coating remains intact and prevents the formation of spinel and rock-salt phases, which eliminates intra-particle cracking of the single-crystal cathode material. These findings demonstrate a potential pathway towards stable and high-performance solid-state batteries during high-voltage operation.

Science & Technology - Other Topics

Fast lithium ion diffusion in brownmillerite Li x Sr 2 Co 2 O 5

Transition metal oxides not only exhibits novel magnetic properties but also provides outstanding ionic transports. Ionic conductors have great potential for interesting tunable physical properties via ionic liquid gating and novel energy storage applications such as all-solid-state lithium batteries. In particular, low migration barriers and high hopping attempt frequency are the keys to achieve fast ion diffusion in solids. Taking advantage of the oxygen-vacancy channel in Li x Sr 2 Co 2 O 5 , we show that migration barriers of lithium ion are as small as 0.28–0.17 eV depending on the lithium concentration rates. Our first-principles calculation also investigated hopping attempt frequency and concluded the room temperature ionic diffusivity and ion conductivity are high as 10 −7 –10 −6 cm 2 s −1 and 10 −3 –10 −2 Scm −1 , respectively, which outperform most of perovskite-type, garnet-type, and sulfide Li-ion solid-state electrolytes. This work proves Li x Sr 2 Co 2 O 5 as a promising super-ionic conductor.

Crystallographic defects