Emerging composite materials are expanding the potential of additive manufacturing and enabling applications previously restricted by traditional manufacturing methods. The multi-phase nature of these composite materials combined with the complex in-ternal geometry of additively manufactured parts have enabled unique behavior, and potentially new applications. Additionally, these materials can be pyrolyzed to create dense metal, ceramic, and glass parts with geometries typically not achievable by tra-ditional processes. Additive manufacturing of borosilicate glass-based systems can open new applications in nuclear engineering, astronomy, and bone regrowth therapy. To elucidate the process-parameter relationship of borosilicate-polylactic acid (PLA) composites, mechanical testing was conducted and compared with a pure polylactic acid polymer baseline. Test specimens were fabricated by fused-filament fabrication with minimal post-processing. Yield strength, ultimate strength, and elastic modulus were calculated from stress-strain curves. Optical and scanning electron microscopy were conducted to observe the specimen microstructure before and after testing. The highest compressive yield strength for the composite was 28.22 MPa, and the highest compressive yield strength for PLA was 49.30 MPa. Print orientation was found to benefit the composite material but have a detrimental effect on the pure matrix material. An elastic modulus of 2.66 GPa was recorded for the borosilicate-PLA composite at 100% infill, 1 shell wall, and layer lines parallel to compression axis. Microscopy revealed that lower modulus composite specimens had the particulates re-distributed within the matrix. Tensile testing was done according to a polymer testing standard, which caused difficulties obtaining consistent fracture within the gauge length.