High Temperature Dielectric Properties and Differential Scanning Calorimetry of Lunar Simulants

To guide development of microwave process technology that could be used during in situ construction on the Moon, we measured the high-temperature basic dielectric properties (εʹ and εʺ) of 17 lunar simulants and related materials. In order to confidently use these data one needs to understand the data’s strengths and weaknesses. Therefore, a goal of this publication is to provide insights into the comparative effects of sample composition, pre-treatments, experimental variables, high temperatures, and other factors on the measured response. The dielectric measurements were performed using the cavity perturbation method over a temperature range between room temperature to 1000 °C, or higher, and provided the real and imaginary components of permittivity at six frequencies. The utility of the original values was limited by the varying density of the pellets used in the measurement. Therefore, all of the εʹ and εʺ measurements at the frequency of 2466 MHz have been scaled to a constant density, 1.75 g/cm 3 . Here the data are presented as graphs chosen to aid analysis within and across simulant groups. To gain additional insight into the processes happening at the elevated temperatures in the dielectric measurements, heat capacity data was obtained using differential scanning calorimetry (DSC) on several of the simulant materials. Our data show that over the frequency range 397 MHz – 2985 MHz a material’s behavior does not greatly change, as compared to the scale of differences observed between lunar mare and highland simulants at high temperatures. For example at 1000 °C, the mare simulant JSC-1A absorbs 10 times more power than the highland simulant NUW-LHT-5M. We observe that as melting temperatures are reached both permittivity and dielectric loss rise non-linearly, helping to explain thermal runaway during microware heating. Our data show that even less than a few weight % of many non-lunar minerals, and the use of mixtures in simulants can affect the dielectric behavior at higher temperatures. A comparison of our results with published dielectric data for Apollo samples and with remote sensing of the Moon supports the conclusion the simulants and lunar material at room temperature have very similar dielectric values.

Differential Scanning Calorimetry

Characterization of Ternary NiTiPt High-Temperature Shape Memory Alloys

Pt additions substituted for Ni in NiTi alloys are known to increase the transformation temperature of the alloy but only at fairly high Pt levels. However, until now only ternary compositions with a very specific stoichiometry, Ni 50-x Pt x Ti 50 , have been investigated and then only to very limited extent. In order to learn more about this potential high-temperature shape memory alloy system, a series of over twenty alloys along and on either side of a line of constant stoichiometry between NiTi and TiPt were arc melted, homogenized, and characterized in terms of their microstructure, transformation temperatures, and hardness. The resulting microstructures were examined by scanning electron microscopy and the phase compositions quantified by energy dispersive spectroscopy. "Stoichiometric" compositions along a line of constant stoichiometry between NiTi to TiPt were essentially single phase but any deviations from a stoichiometry of (Ni,Pt) 50 Ti 50 resulted in the presence of at least two different intermetallic phases, depending on the overall composition of the alloy. Essentially all alloys, whether single or two-phase, still under went a martensitic transformation. It was found that the transformation temperatures were depressed with initial Pt additions but at levels greater than 10 at.% the transformation temperature increased linearly with Pt content. Also, the transformation temperatures were relatively insensitive to alloy stoichiometry within the range of alloys examined. Finally, the dependence of hardness on Pt content for a series of Ni 50-x Pt x Ti 50 alloys showed solution softening at low Pt levels, while hardening was observed in ternary alloys containing more than about 10 at.% Pt. On either side of these "stoichiometric" compositions, hardness was also found to increase significantly.

Transformation Temperatures

Properties and Potential of Two (Ni,Pt)Ti Alloys for Use as High-Temperature Actuator Materials

The microstructure, transformation temperatures, basic tensile properties, shape memory behavior, and work output for two (Ni,Ti)Pt high-temperature shape memory alloys have been characterized. One was a Ni 30 Pt 20 Ti 50 alloy (referred to as 20Pt) with transformation temperatures above 230 °C and the other was a Ni 20 Pt 30 Ti 50 alloy (30Pt) with transformation temperatures above 530 °C. Both materials displayed shape memory behavior and were capable of 100% (no-load) strain recovery for strain levels up to their fracture limit (3-4%) when deformed at room temperature. For the 20Pt alloy, the tensile strength, modulus, and ductility dramatically increased when the material was tested just above the austenite finish (A f ) temperature. For the 30Pt alloy, a similar change in yield behavior at temperatures above the A f was not observed. In this case the strength of the austenite phase was at best comparable and generally much weaker than the martensite phase. A ductility minimum was also observed just below the A s temperature in this alloy. As a result of these differences in tensile behavior, the two alloys performed completely different when thermally cycled under constant load. The 20Pt alloy behaved similar to conventional binary NiTi alloys with work output due to the martensite-to-austenite transformation initially increasing with applied stress. The maximum work output measured in the 20Pt alloy was nearly 9 J/cm 3 and was limited by the tensile ductility of the material. In contrast, the martensite-to-austenite transformation in the 30Pt alloy was not capable of performing work against any bias load. The reason for this behavior was traced back to its basic mechanical properties, where the yield strength of the austenite phase was similar to or lower than that of the martensite phase, depending on temperature. Hence, the recovery or transformation strain for the 30Pt alloy under load was essentially zero, resulting in zero work output.

High-Temperature Shape Memory Alloy