Graphitization of banana peel – synergistic effect of Ca and other elements of the biomass on carbon structure transformation

Recently, growing interest has been observed in using calcium as an effective catalyst for graphitizing disordered carbon materials derived from biomass and bioprecursors, such as cellulose and lignin, at relatively low tem peratures (<2000 °C). Herein, it is demonstrated that in the presence of elements such as calcium, silicon, sulfur, and potassium, which are abundant in banana peel composed of cellulose and lignin base, graphitization occurs much more effectively. The addition of external calcium source, in the form of calcium carbonate, to the banana peel-derived carbon and heat-treatment of the mixture under protective atmosphere up to 1750 °C results in a significant increase in the degree of the graphitization order and local formation of graphite crystals, whereas the same preparation and heat-treatment procedure applied to carbon material derived from pristine cellulose does not lead to such effective graphitization. It is indicated that the graphitization of banana peel carbon occurs due to the synergistic effect of the external Ca-based catalyst and the internal elements present in the raw biomass, supporting the transformation of the disordered graphene-like layers into graphitic structures. These findings are important for the future production of green graphite from biomass

09 BIOMASS FUELS↗

DOE OSTI2026

Optimizing Porous Transport Layer Porosity for Proton Exchange Membrane Water Electrolysis

An empirical model is presented that describes anode-side losses related to porous transport layer (PTL) morphology in proton exchange membrane water electrolysis (PEMWE). The model is based on an advanced voltage breakdown analysis that links various overpotentials to PTL morphology. Custom Ti PTLs, spanning uncommonly low porosities (22 - 31%), were fabricated and analyzed with X-ray CT to obtain pore and particle size distributions. Particle size distributions were consistent across samples with an average particle diameter of 12.0?..mu..m, whereas average pore diameters ranged from 6.0 to 7.0?..mu..m. The PTLs were tested in standard PEMWE cell assemblies with anode catalyst loadings of 0.1 mgIr cm-2 to obtain polarization curves, electrochemical impedance spectra, and augmented Tafel analysis. The PTL-dependent anode side losses were deconvoluted and assigned to excess utilization, concentration, ion transport resistance, and electrical contact resistance overpotentials. The data and model reveal an optimal 20 - 28% PTL porosity region where utilization and contact resistance overpotentials are minimized without triggering concentration and ion transport losses related to water deprivation. The optimal PTL porosity depends on the operating current density and is demonstrated at realistic PEMWE water flow rates to establish PTL design guidance for operation at scale.

08 HYDROGEN↗

DOE OSTI2026

Effect of directed energy deposition process parameter on build quality of tantalum

Tantalum is a refractory metal used in a variety of harsh environment applications. Additive manufacturing of tantalum is limited based on its high melting point and affinity for oxygen. Directed Energy Deposition is an additive manufacturing technique with rapid deposition time and compositional flexibility within builds. Additively manufactured tantalum is susceptible to a variety of material and process-based defects. Various lack-of-fusion defects were identified resulting from excessive powder feed rates or insufficient laser power. Oxygen impurities in some samples caused cracking and increased material hardness. Precipitates were identified in the highly oxidized samples which were printed immediately after the build chamber was opened. High-density, low-defect parts were successfully produced. The effects of scan speed, laser power, and powder feed rate on density and defects were analyzed. A processing window was identified for producing high-quality parts which requires adequately high laser power and lower powder feed rate.

DED↗

NASA NTRS2026

Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherents

Certification of adhesively bonded structures is currently a challenge for aircraft manufacturers. The ability to certify bonds in primary structure can reduce dependence on fasteners and this will enable more efficient manufacturing. For example, drilling holes and installing fasteners in bonded joints can be a potentially significant bottleneck in airframe manufacturing. In addition, fasteners increase the airframe weight and can add stress concentration areas. Reducing fastener count can accelerate manufacturing and improve aircraft performance. NASA is currently investigating nondestructive evaluation (NDE) techniques to assess bond integrity. For example, bond thickness influences bond strength and therefore NDE techniques are being investigated to determine bond thickness. For bonded metal structures, there is a large difference in the thermal diffusivity between the 7075 aluminum alloy metal adherends and aircraft grade adhesive. Multi-layered thermal models show a large variation in the thermal response for bondline adhesive thicknesses that vary from 100 to 300 microns for adherend thicknesses of 0.163 cm. Experimental through-transmission thermal measurements reveal promise to quantitatively characterize the bondline thickness. Results were validated with X-ray computed tomography and optical microscopy measurements, and influence of porosity on the thermal model and measurements are investigated.

bondline thickness↗

NASA NTRS2026

Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherends

Certification of adhesively bonded structures is currently a challenge for aircraft manufacturers. The ability to certify bonds in primary structure can reduce dependence on fasteners and this will enable more efficient manufacturing. For example, drilling holes and installing fasteners in bonded joints can be a potentially significant bottleneck in airframe manufacturing. In addition, fasteners increase the airframe weight and can add stress concentration areas. Reducing fastener count can accelerate manufacturing and improve aircraft performance. NASA is currently investigating nondestructive evaluation (NDE) techniques to assess bond integrity. For example, bond thickness influences bond strength and therefore NDE techniques are being investigated to determine bond thickness. For bonded metal structures, there is a large difference in the thermal diffusivity between the 7075 aluminum alloy metal adherends and aircraft grade adhesive. Multi-layered thermal models show a large variation in the thermal response for bondline adhesive thicknesses that vary from 100 to 300 microns for adherend thicknesses of 0.163 cm. Experimental through-transmission thermal measurements reveal promise to quantitatively characterize the bondline thickness. Results were validated with X-ray computed tomography and optical microscopy measurements, and influence of porosity on the thermal model and measurements are investigated.

X-ray computed tomography↗

DOE OSTI2025

A General Solution Route to Nanoporous Metal Oxide Films

Metal oxide semiconductors are of interest as efficient, stable, and low-cost photoanode materials for photoelectrochemical water splitting, but their characteristically poor charge transport properties remain a fundamental challenge to practical use. Nanoporous metal oxide films that feature open bicontinuous networks of nanocrystals and nanopores can overcome such inefficient charge transport to enable high-performance photoanodes. Here, this paper describes a general method to make high-quality nanoporous films of metal oxides by spin coating and calcining molecular inks that contain a porosity-generating block copolymer. Phase-pure nanoporous films of BiFeO 3 , FeWO 4 , WO 3 , Fe 2 O 3 , and TiO 2 serve to demonstrate the versatility of the approach. It is demonstrated that the crystallite size, film porosity, and film thickness can be independently tuned by adjusting the ink composition and film processing conditions. The method is extended to fabricate core–shell nanoporous films consisting of a nanoporous film coated in a thin shell of a second metal oxide, using WO 3 –BiVO 4 and BiFeO 3 –BiVO 4 as examples. Given its simplicity and flexibility, this solution-phase route should prove useful for making nanoporous films of many different materials for a variety of applications, including energy conversion and storage, catalysis, and chemical sensing.

coating materials↗