DOE OSTI2025

Ultra-high temperature testing and performance of L-PBF C103

Additive Manufacturing (AM) of refractory alloys is gaining traction as a materials processing route for components subject to extreme temperature environments. Due to the low oxidation resistance of refractory alloys, novel methods for evaluating their elevated temperature performance must be developed. In this work, a Gleeble® 3800 thermomechanical load frame was modified to evaluate the mechanical properties of laser powder bed fusion (L-PBF) consolidated niobium alloy C103 ranging from room temperature (RT) to 1400 °C. The fixturing and sample geometry were designed to accommodate Joule heating and prevent damage to the test chamber. Oxidation of the samples was minimized via testing in vacuum level of 1E-5 Torr. Ultimate tensile strength (UTS), yield strength (YS), elongation, and strain-hardening behavior were determined as a function of temperature. L-PBF C103 presented an average UTS of ∼650 MPa and over 25 % elongation at RT. Above RT, the UTS and YS dropped then leveled off from 500 °C to 1000 °C with values ranging from ∼400 MPa to ∼460 MPa, which is consistent with dynamic strain aging observed in this class of alloys. The strength rapidly declined after 1200 °C to ∼150 MPa at 1400 °C. Fractography indicated ductile fractures for the C103 at all test temperatures, and Electron Backscatter Diffraction (EBSD) analysis revealed a textured microstructure and the presence of dynamic recrystallization within the necked region of the sample tested at 1400 °C.

33 ADVANCED PROPULSION SYSTEMS↗
DOE OSTI2026

Influence of rolling reduction and annealing on recrystallization and grain structure in Ta-2.5W alloys

The microstructural evolution of wrought Tantalum - 2.5 wt% Tungsten (Ta-2.5W) alloys during thermomechanical processing is critical for optimizing their mechanical reliability in demanding applications such as aerospace, chemical processing, and nuclear technology. Despite the widespread use of Ta-W alloys, a comprehensive understanding of how rolling reduction, annealing temperature, and elemental inhomogeneity interact to determine recrystallization behavior and grain refinement remains incomplete. Here, in this study, we systematically investigate the effects of cold rolling and subsequent annealing on the microstructure of Ta-2.5W, with particular attention to grain orientation, stored energy, and elemental banding. Our results demonstrate that higher rolling reduction rates lower the onset and completion temperatures for recrystallization, resulting in finer and more homogeneous grain structures. Electron backscatter diffraction (EBSD) analysis reveals that grains with a 〈111〉 parallel to the plate normal possess higher stored energy and nucleate recrystallization more readily than grains with a 〈001〉 parallel to the plate normal. Elemental mapping shows that tungsten inhomogeneity leads to localized bands of accelerated recrystallization and hardness variation. These findings provide new insights into the mechanisms of microstructure refinement in Ta-2.5W alloys, offering guidance for tailoring processing routes to achieve superior performance in demanding engineering environments.

Annealing↗
DOE OSTI2020

In-situ visualization of corrosion behavior of Al CoCrFeNi high-entropy alloys during electrochemical polarization

In this study, the corrosion behavior of the Al x CoCrFeNi (x = 0.3, 0.5, 0.7) high-entropy alloys (HEAs) is investigated by an in-situ visualization system. Surface morphology changes on both micro-spatial and temporal scales are monitored in the 3.5 wt% NaCl solution during the potentiodynamic polarization. The microstructures of the Al x CoCrFeNi HEAs are characterized by SEM, EBSD, and EDS. The results show that the microstructure evolves from singe face-centered cubic (FCC) phase to multi-phases by increasing the Al content. The in-situ observations directly reveal the different localized corrosion processes in the AlxCoCrFeNi HEAs. In the single FCC phase Al 0.3 CoCrFeNi HEA, localized corrosion shows in the form of pitting. In the Al 0.5 CoCrFeNi and Al 0.7 CoCrFeNi alloys, which possess FCC and body-centered cubic (BCC) phases, the localized corrosion initiates and propagates in the Cr-depleted BCC phase. In addition, the in-situ visualization uncovers the evolution of current serration, which represents the propagation and repassivation of metastable pit during the polarization. The frequent occurrence of metastable pits indicates distinct repassivation ability of the Al 0.3 CoCrFeNi HEA.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Investigation of phase-transformation path in TiZrHf(VNbTa)x refractory high-entropy alloys and its effect on mechanical property

Refractory high-entropy alloys (RHEAs) show a great potential as structural materials due to their remarkable properties, such as high strength and thermal stability. Despite these advantages, the RHEAs still suffer from the limited ductility at room temperature. To overcome the strength-ductility trade-off, the new RHEA design strategy, transformation-induced plasticity (TRIP) HEAs, have been developed by applying metastability-engineering approach. With the newly developed RHEAs design strategy, we designed metastable RHEAs, TiZrHfVxNbxTax (x = 1.0, 0.5 and 0.1) with decrease of the β-stabilizing elements (V, Nb, and Ta) to promote the transformation-induced ductility and work-hardening capability. The proper addition of the β-stabilizing elements (V, Nb, and Ta) into the ternary equi-molar TiZrHf alloy (TiZrHfV 0.1 Nb 0.1 Ta 0.1 ) leads to stress/strain-induced phase transformation from the body-centered cubic (BCC) to hexagonal-close-packed (HCP) α' and/or orthorhombic α" phases. Here, detailed studies on the phase transformation sequence during the deformation were carried out using X-ray diffraction (XRD), electron back-scattered diffraction (EBSD), and transmission-electron microscope (TEM), which revealed the stepwise phase transformation that is responsible for the strong strain hardening behavior. Furthermore, we further suggested the new transformation-induced-plasticity (TRIP) HEA design strategy, applying the Bo-Md approach.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Directed energy deposition of radially functionally graded nickel based superalloys IN625 and IN738: Microstructure and mechanical properties

This study investigates the microstructure and mechanical properties of radially functionally graded (RFG) materials fabricated from nickel-based superalloys IN625 and IN738 using directed energy deposition (DED). RFG cylindrical deposits with radial gradients of IN625-IN738 and IN738-IN625 were successfully fabricated and confirmed to be crack-free through tailored composition grading, scan strategy and process parameters that minimized thermal gradients and solidification velocities. Microstructural analysis revealed distinct variations across the gradient, characterized by differences in dendrite arm spacing, microsegregation, and the formation of distinct γ' precipitates and carbide/boride phases (MC, M 6 C, M 2 C, and MB 2 ) in as-deposited (AD) conditions, which evolved into M 23 C 6 and M 2 B upon subsequent heat treatment (HT). EBSD showed predominant columnar grains with a [100] texture, while microhardness profiles demonstrated consistent variation across the gradients. Mechanical testing highlighted the synergy of the graded structure, combining IN738's strength with IN625's ductility, resulting in enhanced properties such as a yield strength of 1131 MPa, ultimate tensile strength of 1382 MPa, and elongation of 12 % for HT IN625-IN738 grading. Numerical simulations employing CALPHAD thermodynamic calculations and finite element thermal modeling are used to establish phase evolution and microstructural feature correlation with thermal profiles, aiding in the optimization of process-structure-property relationship.

Additive manufacturing↗
DOE OSTI2024

Parameter development and characterization of laser powder directed energy deposition of Nb – Alloy C103 for thin wall geometries

This work focuses on the parameter development and microstructural characterization of Nb-based alloy C103 for thin wall structures produced via laser powder – directed energy deposition (LP – DED). Laser power and scanning speeds were varied as part of a design of experiments to identify adequate print parameters. Combinations were evaluated for relative density, porosity, and geometrical accuracy. A combination of a laser power of 1420 W and scanning speed of 14 mm/s resulted in a relative density >99%, exhibited a consistent weld bead profile and was used for further microstructural evaluation. A mix of optical and scanning electron microscopy (SEM) revealed small, slightly elongated grains along the edges and large epitaxial grains in the central region along the Build – Transverse view. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) analysis revealed Hf rich columnar cells in the center that transition into an evenly spaced cellular structure towards the edges of the built sample. Electron backscatter diffraction (EBSD) scans show a sharp [001] texture when looking at the cross section of the sample along the build direction. The Build – Scan view revealed a zig – zag pattern that follows the back – and – forth deposition strategy that was used. Finally, microhardness measurements were taken in the as – built (AB) and stress relieved (SR) conditions to baseline preliminary mechanical properties. The AB condition exhibited a large amount of scatter in the data and averages up to 11% larger than the SR condition. The reduction in scatter upon applying the SR cycle are indicative of a large concertation of dislocations present in the AB condition.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Strength-ductility synergy through microstructural and compositional heterogeneity in directed energy deposition additive manufacturing of face-centered cubic materials

Directed energy deposition (DED) is an additive manufacturing (AM) process based on welding technology and offers the advantages of large build volume, high deposition rate, and ability to fabricate multi-material parts. Epitaxial continuous columnar grain growth is a characteristic microstructural feature of DED processed alloys. In this study, a bamboo-like microstructure (periodic alternation of equiaxed and columnar structure) was produced by adopting an intermittent deposition strategy in 316L stainless steel and Inconel 625. The formation of a bamboo-like alternating microstructure was confirmed through electron backscattered diffraction (EBSD) analysis. Hardness mapping showed that the columnar to equiaxed transition (CET) occurred at the region right below the fusion line. A finite element (FE) model was used to investigate the relationship between the temperature gradient (G) and the solidification rate (R). The FE model showed a low G/R ratio at the region right below the interface promoting the CET. The grain size and material-dependent deformation behaviors are analyzed using digital image correlation (DIC). The lower deformation on the fine-grain regions observed in DIC analysis is attributed to a higher strain hardening rate, which is confirmed through dislocation density analysis on a tensile-interrupted specimen. The periodically alternating grain size coupled with the microstructural changes caused by intermittent deposition strategy result in a better strength-ductility synergy in both single-material and bimetallic specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Binder-jetted AISI M2 tool steel during hot isostatic pressing: Densification and carbide transformation

Binder jetting (BJ) enables fabrication of complex components from high-alloy steels such as AISI M2; however, residual porosity after sintering limits mechanical performance. This study investigates the coupled effects of binder chemistry, sintering conditions, cooling rate, and subsequent hot isostatic pressing (HIP) on densification, microstructure, and mechanical response in binder-jetted M2 tool steel. HIP increased relative density from ∼93 to 95% to >99% and improved compressive strength by ∼40-70%. Densification was governed by initial pore morphology, where closed porosity was effectively eliminated, while interconnected porosity limited full consolidation. Microstructural analysis (XRD, EBSD, SEM) shows that HIP promotes dissolution of metastable carbides and redistribution of alloying elements (W, Mo, V), transforming heterogeneous carbide networks into finer and more uniformly distributed M 2 C, MC, and M 6 C phases through diffusion-assisted homogenization. Among the investigated conditions, the FluidFuse binder combined with sintering at 1270 °C for 60 min and furnace cooling produced the most balanced response, achieving ∼99.7% density, ∼855 HV hardness, ∼4130 MPa compressive strength, and ∼24% strain. In contrast, higher sintering temperatures promoted carbide coarsening, reducing ductility despite high density. HIP reduces microstructural heterogeneity and drives the system toward a near-equilibrium state with reduced sensitivity to prior processing history. A comparative assessment with conventional and additive manufacturing routes (LPBF, DED, EBM, FFF) shows that the BJ-HIP approach achieves competitive densification and mechanical performance. These findings provide a mechanistic basis for controlling densification and microstructure in high-alloy steels processed via BJAM.

AISI M2 tool steel↗
DOE OSTI2021

Thermal stability of additively manufactured austenitic 304L ODS alloy

Thermal stability and high-temperature mechanical properties of a 304L austenitic oxide dispersion strengthened (ODS) alloy manufactured via laser powder bed fusion (LPBF) are examined in this work. Additively manufactured 304L ODS alloy samples were aged at temperatures of 1000, 1100, and 1200 °C for 100 h in an argon atmosphere. Microstructure characterization of LPBF 304L ODS alloy before and after the thermal stability experiments revealed that despite the annihilation of dislocations, induced cellular substructure by the LPBF process was partially retained in the ODS alloy even after aging at 1200 °C. The size of Y-Si-O nanoparticles after aging at 1200 °C increased from 25 to 50 nm. EBSD analysis revealed that nanoparticles retained the microstructure of LPBF 304L ODS and hindered recrystallization and further grain growth. At 600 °C and 800 °C, the yield stress of the 290 and 145 MPa were measured, respectively, which are substantially higher than 113 MPa, and 68 MPa for 304L at the same temperatures. Furthermore, the creep properties of LPBF 304L ODS alloy were evaluated at a temperature of 700 °C under three applied stresses of 70, 85, and 100 MPa yielding a stress exponent (n) of ~7.7; the minimum creep rate at 100 MPa was found to be about two orders of magnitude lower than found in the literature for wrought 304L stainless steel.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Origins of high ductility exhibited by an extruded magnesium alloy Mg-1.8Zn-0.2Ca: Experiments and crystal plasticity modeling

Low ductility and strength are major bottlenecks against Mg alloys' wide applications. In this work, we systematically design the composition and fabrication process for a low-alloyed Mg-Zn-Ca alloy, showing that it can be extruded at low temperatures (~ 250 degrees C) and high speeds (~2 mm/s). After the extrusion, this alloy exhibits a substantially weakened basal texture, relatively small grain size, very high tensile elongation (~ 30%), and good strength. The origin of the considerably improved ductility was studied using a combination of three-dimensional atom probe tomography (3D-APT), transmission electron microscopy (TEM), electron backscattered diffraction (EBSD) in conjunction with surface slip trace analysis, in-situ synchrotron X-ray diffraction, and elasto-plastic self-consistent (EPSC) modeling. Co-segregation of Zn and Ca atoms at a grain boundary is observed and associated with texture weakening and grain boundary mediated plasticity, both improving the ductility. While basal slip and prismatic slip are identified as the dominant deformation systems in the alloy, the ratio between their slip resistances is substantially reduced relative to pure Mg and most other Mg alloys, significantly contributing to the improved ductility of the alloy. This Mg-Zn-Ca alloy exhibiting excellent mechanical properties and low fabrication cost is a promising candidate for industrial productions.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Quantification of silicon carbide grain structure in TRISO fuel by BSE image analysis

The grain structure of the silicon carbide (SiC) layer in tristructural-isotropic (TRISO) fuels has commonly been qualified in fuel specifications based on a qualitative comparison to visual standards to ensure undesirable microstructure are not produced. This approach is inherently dependent on subjective judgement and provides limited data for analysis or comparison. An alternative method to rapidly quantify (i.e., provide a numeric measure of) the grain structure of the SiC layer in TRISO fuels has been developed. This method relies on the identification of silicon carbide grain boundaries based on brightness variation in backscattered electron (BSE) images through the application of automated image processing algorithms. The speed with which the requisite BSE imaging and analysis may be completed enables the practical use of this method on an industrial scale as a part of qualifying TRISO fuel to meet a given specification on silicon carbide grain structure, which is an important parameter for TRISO fuel performance. The method is benchmarked by comparison to prior Electron-Backscattered Diffraction (EBSD) results for TRISO particles from the Advanced Gas Reactor (AGR) program.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

A study on texture stability and the biaxial creep behavior of as-hydrided CWSR Zircaloy-4 cladding at the effective stresses from 55 MPa to 65 MPa and temperatures from 300°C to 400°C

The creep rupture of high burnup used nuclear fuel (> 45 GWD/MTU) cladding is regarded as one of the failure mechanisms during long-term dry storage. A high amount of zirconium hydride in the cladding matrix would degrade the mechanical properties of the cladding especially leading to delayed hydride cracking. To better understand the influence of zirconium hydride on the biaxial thermal creep performance and the crystalline texture stability of Zircaloy-4 cladding, the pressurized tube technique is applied to test the durability of the as-hydrided material. Tests were performed on as-received Zircaloy-4 tubular specimens as well as-hydrided ones with targeted 300 wt parts per million (wppm) or 750 wppm hydrogen. The biaxial creep experiments were conducted at temperatures from 300 degrees C to 400 degrees C and at equivalent stresses at mid-wall from 55 MPa to 65 MPa. The hydridation process prior to creep tests induces the formation of FCC delta-hydride platelets along the circumferential direction of the tube. This alignment and phase structure of hydride show no significant change after biaxial creep tests. The creep strain-rate negatively depends on the hydrogen content. The synchrotron wide-angle X-ray diffraction (WAXD) technique and electron backscatter diffraction (EBSD) analysis were applied for the study of the crystallographic orientation relationship. zirconium-to-hydride grain orientation follows Shoji-Nishiyama crystallographic relationship. This relationship is stable before and after creep deformation. These results of creep performance and texture stability of Zircaloy-4 claddings can help support the design basis of interim and long-term dry storage facilities.

creep↗
DOE OSTI2024

Characterization of fluidized bed chemical vapor deposition ZrC coatings on PyC/YSZ kernels deposited under differing conditions

In this study, coated fuel particle architectures with ZrC coatings are candidate fuels for advanced power reactors and space nuclear propulsion (SNP) concepts. Owing to its relevance to SNP, the composition, microstructure, and mechanical properties of eight ZrC coatings prepared by fluidized bed chemical vapor deposition were evaluated. Evaluation by SEM and EBSD showed that all grains were columnar. Across the various examined samples, minor axis diameters varied between 0.3 and 1.1 μm, and major axis diameters varied between 0.4 and 2.3 μm. Major and minor diameters increased with thickness particularly at higher deposition temperatures in which the major grain axis (from an ellipse fit to the grain shape) increased by 2.5 μm over the entire coating. Coatings with higher reactive gas flows and Zr/C concentrations closer to 1 were observed to contain nanocrystalline graphite deposits. Reactive gas flow doubling led to increases in coating thickness from around 10–15 μm to around 22–27 μm.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2026

A comparison of wrought and powder metallurgical FeCrAl claddings under simulated LWR accident transients

Iron-chromium-aluminum (FeCrAl) alloys are potential accident tolerant fuel (ATF) cladding candidates for light-water reactors but are difficult to fabricate as thin-walled tubes via conventional cast-and-wrought routes. Powder metallurgy (PM) offers a manufacturing alternative with improved compositional control, but its transient accident performance has not been directly benchmarked against wrought variants. This study evaluates the burst behavior of commercially developed PM-processed FeCrAl alloys, PM-C26M (Fe-12Cr-6Al-2Mo) and the high precipitate density FA-SMT (Fe-22Cr-5Al-3Mo), under simulated light-water reactor accident transient conditions. Burst testing was conducted using the Severe Accident Test Station with heating rates of 5 °C/s and 50 °C/s and internal pressures ranging from 25 MPa to 100 MPa. PM-C26M reproduced wrought C26M burst behavior within 7–37 °C across the stress range, indicating that PM processing does not compromise transient strength. FA-SMT exhibited markedly higher burst temperatures and reduced heating-rate sensitivity, consistent with its engineered precipitate strengthening. FA-SMT rupture exhibited axial "unzipping" rather than the lateral tearing characteristic of PM- and wrought C26M. Post-test EBSD and fractography indicate that this behavior is strongly correlated with strain-gated intergranular void nucleation associated with the dense precipitate architecture of FA-SMT, a response absent in the comparatively clean PM-C26M matrix and consistent with rupture morphologies reported for oxide-dispersion strengthened (ODS) FeCrAl of similar base-matrix chemistry to PM-C26M. These findings highlight the potential of powder metallurgy as a viable fabrication route for ATF claddings from an accident performance standpoint.

Bell, Sam [ORNL] (ORCID:0000000251905657)↗
DOE OSTI2020

Effect of aging on failure mechanism of Alloy 709 at various temperatures

Alloy 709 is a novel austenitic stainless steel with high temperature creep strength, weldability, and corrosion resistance. These properties make the material suitable for applications in the structure of next-generation nuclear power plants. Enduring high temperatures for an extended period of time in the harsh environments of a nuclear power plant results in thermal aging of the material. Therefore, it is imperative to study the effect of thermal aging on the microstructure and mechanical properties of Alloy 709 before its application in the next generation power plants. In this study, hot-processed (forged + rolled), annealed and quenched ingots of Alloy 709 are aged at 650 °C for 2000 h in air and then tested at various temperatures up to 850 °C in an in-situ heating-loading Scanning Electron Microscope (SEM) equipped with Energy Dispersive Spectroscopy (EDS) and Electron Backscatter Diffraction (EBSD). The effect of testing temperature and aging on microstructural evolutions during tensile testing of as-received and aged samples are studied. Furthermore, both as-received and aged samples displayed serrations and drop in ductility at elevated temperatures, due to the effect of dynamic strain aging (DSA). The occurrence of DSA activity was found within temperatures range of 500 °C–750 °C in as-received and 550 °C - 650 °C in aged samples. The aged samples showed less elongation accompanied by shallower dimples on the fractured surface, indicating less ductile failure mechanism compared to as-received samples. Failure mechanism observations on the fracture surface using SEM fractography are correlated to the observations made on the sample surface using in-situ SEM to achieve a complementary set of information to better understand the failure mechanism of this novel alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2021

A study on the creep behavior of alloy 709 using in-situ scanning electron microscopy

In this research, an experimental evaluation of creep properties of Alloy 709 in the temperature range of 750–850 °C was undertaken. Alloy 709 is a novel austenitic stainless steel with 20% Cr and 25% Ni by wt% that was developed for application in structural components of nuclear power plants. Creep rupture tests were conducted in an in-situ heating-loading and Scanning Electron Microscope (SEM) unit equipped with Electron Backscatter Diffraction (EBSD) detector and Energy Dispersive Spectroscopy (EDS). “Real-time” creep damage mechanisms of Alloy 709 at various stresses and temperatures using a flat, un-notched sample with continuously reducing cross-section is studied so that the failure and maximum creep damage occurred at the center of the sample where the in-situ SEM imaging could be focused. Accelerated creep tests at temperatures and stresses above service conditions were performed by employing multiple blocks of constant loads where the loads were increased once the sample attained constant creep rate, indicating a secondary creep regime. This technique ensures multiple data points can be obtained from the same test, saves the time required for an otherwise long-term creep test and usage of SEM. Further, Coincident Site Lattice (CSL) boundary maps were collected as control maps before testing, and the grain boundaries were observed during the creep test to understand the effect of grain boundary character on the creep damage mechanism. Void growth, grain boundary separation, and sliding were found to be the main creep mechanisms whose rate is dependent on stress and temperature. Failure mechanisms studied on the fracture surface using SEM fractography were correlated to the sample surface observations to create complementary information to better understand the underline creep mechanism of Alloy 709.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Reconstructing parent microstructures in martensitic and pearlitic Ti-Cu

Evaluating the microstructural evolution of parent phases has long been a challenge in metals with a partial or complete solid state transformation. Most parent microstructure evolution has to be inferred from the product microstructure, with some information permanently lost. Parent microstructure reconstructions relying on orientation relationships and EBSD data are a useful tool to overcome this challenge, though much background knowledge is required to do so. Here, this work introduces a reconstruction process for a eutectoid composition Ti-Cu binary alloy to evaluate the high temperature β-Ti phase from martensitic and pearlitic product microstructures. Martensitic microstructures were accurately reconstructed, enabling elucidation of β-Ti grain size and texture, and the employed script included for scientific reference. Pearlitic microstructures did not reconstruct effectively with the current process. However, new insight into the interfacial crystallographic orientations of pearlitic Ti-Cu microstructures was gleaned via this analysis, and future investigations of interest are discussed accordingly. Ultimately, these findings demonstrate tools widely implemented on conventional titanium and ferrous alloys can also be applied to understand parent microstructures in Ti-Cu and other alloys of emerging interest. This is especially of use as new manufacturing processes for such materials require understanding how parent phase microstructures respond to new, novel material processing such as AM.

36 MATERIALS SCIENCE↗