NASA NTRS1976

Comparison of type A and C Fluorinated Ethylene Propylene (FEP) as cover materials for silicon solar cells

Fluorinated ethylene propylene film (FEP, 0.0127 cm thick) was heat and pressure laminated to silicon solar cells as a low cost substitute for quartz covers. The FEP-C, treated on one side for bonding, was compared to FEP-A, an untreated FEP. With FEP-A, a silane adhesion promoter was applied to the cells. The FEP-C covers delaminated during accelerated temperature-humidity testing and Earth environmental exposure testing; FEP-A covers were unchanged. No differences were observed in peel tests, but FEP-A is superior in its resistance to tearing and in retention of transmission properties after exposure to ultraviolet radiation.

Broder, J. D.↗
NASA NTRS1975

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 108 graphite-epoxy spoilers on 737 transport aircraft, and related ground-based environmental exposure of graphite-epoxy material specimens were evaluated. Four spoilers were installed on each of 27 aircraft for a 5-year study. As of February 28, 1975, a total of 294,280 spoiler flight-hours and 460,686 spoiler landings were accumulated. Based on visual, ultrasonic, and destructive testing, no moisture migration into the honeycomb core and no core corrosion has occurred. Tests of removed spoilers and of ground-based exposure specimens after the first year of service indicate no significant changes in composite strength.

Stoecklin, R. L.↗
NASA NTRS1976

Residual stresses in polymer matrix composite laminates

Residual stresses in composites are induced during fabrication and by environmental exposure. The theory formulated can describe the shrinkage commonly observed after a thermal expansion test. Comparison between the analysis and experimental data for laminates of various material systems indicates that the residual stress-free temperature can be lower than the curing temperature, depending on the curing process. Effects of residual stresses on ply failure including the acoustic emission characteristics are discussed.

Hahn, H. T.↗
NASA NTRS1977

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 110 graphite epoxy spoilers on 737 transport aircraft was reviewed as well as ground based environmental exposure of graphite epoxy material specimens for the period from April 1976 through April 1977. Several spoilers were installed on each of 27 aircraft representing seven major airlines operating throughout the world. A flight service evaluation program of at least 5 years is under way. As of April 30, 1977, a total of 766,938 spoiler flight hours and 1,168,090 spoiler landings were accumulated by the fleet. Based on visual ultrasonic, and destructive testing, there was no evidence of moisture migration into the honeycomb core and no core corrosion. Tests of removed spoilers and of ground based exposure specimens after the third year of service continue to indicate modest changes in composite strength properties.

Stoecklin, R. L.↗
NASA NTRS1976

The 737 graphite composite flight spoiler flight service evaluation

The flight-service experience of 110 graphite-epoxy spoilers on 737 transport aircraft and related ground-based environmental exposure of graphite-epoxy material specimens is reported. Spoilers were installed on each of 27 aircraft representing seven major airlines operating throughout the world. Based on visual, ultrasonic, and destructive testing, there is no evidence of moisture migration into the honeycomb core and no core corrosion. Tests of removed spoilers and of ground-based exposure specimens after the second year of service indicate modest changes in composite strength.

Stoecklin, R. L.↗
NASA NTRS1976

Third Conference on Fibrous Composites in Flight Vehicle Design, part 1

The use of fibrous composite materials in the design of aircraft and space vehicle structures and their impact on future vehicle systems are discussed. The topics covered include: flight test work on composite components, design concepts and hardware, specialized applications, operational experience, certification and design criteria. Contributions to the design technology base include data concerning material properties, design procedures, environmental exposure effects, manufacturing procedures, and flight service reliability. By including composites as baseline design materials, significant payoffs are expected in terms of reduced structural weight fractions, longer structural life, reduced fuel consumption, reduced structural complexity, and reduced manufacturing cost.

Source record↗
NASA NTRS1978

SEASAT A satellite scatterometer

The analyses performed in the early period of the program which formed the basis of the sensor design is reviewed, along with the sensor design. The test program is outlined, listing all tests performed and the environmental exposure (simulated) for each, as applicable. Ground support equipment designed and built for assembly integration and field testing is described. The software developed during the program and the algorithms/flow diagrams which formed the bases for the software are summarized.

Bianchi, R.↗
NASA NTRS1979

Environmental effects on space shuttle reusable surface insulation coated with reaction cured glass

Sample titles of the space shuttle reusable surface insulation was subjected alternately to simulated mission heating and either real or simulated environmental exposure for up to 34 cycles. The coating cracked as a result of exposure to high temperature and moisture conditions, and insulation with cracked coatings absorbed significant quantities of water in the launch-pad environment. Cracking was a complex function of time, temperature, and moisture exposure. Cracked coatings remained adherent to the insulation for up to 24 cycles past initial cracking.

Ransone, P. O.↗
NASA NTRS1980

Qualification test results for DOE solar photovoltaic flat panel procurement - PRDA 38

Twelve types of prototypes modules for the DOE Photovoltaic Flat Panel Procurement (PRDA 38) were subjected to qualification tests at the Jet Propulsion Laboratory according to a new specification. Environmental exposures were carried out separately and included temperature cycling, humidity, wind simulation, and hail. The most serious problems discovered were reduced insulation resistance to ground and ground continuity of the metal frames, electrical degradation, erratic power readings, and delamination. The electrical and physical characteristics of the newly received modules are also given.

Griffith, J. S.↗
NASA NTRS1982

The 737 graphite composite flight spoiler flight service evaluation

A flight service report was prepared which covers the flight service experience of 111 graphite epoxy spoilers on 737 transport aircraft and related ground based environmental exposure of graphite epoxy material specimens. Spoilers were installed on 28 aircraft representing seven major airlines operating throughout the world. Tests of removed spoilers after the seventh year of service continue to indicate modest changes in composite strength properties. Two spoilers were tested, one with 6 and one with 7 years of service, and both had residual strengths that fall within the original static strength scatter band. Both these units had typical service included discrepancies when tested. Based on visual, ultrasonic, and destructive inspection there continues to be no evidence of moisture migration into the honeycomb core and no core corrosion in the deployed units.

Coggeshall, R. L.↗
NASA NTRS1981

Warping of unsymmetric cross-ply graphite/epoxy laminates

Warping in unsymmetric graphite/epoxy laminates was studied with particular attention given to the change of residual stresses resulting from long term environmental exposure. Square, cured prepreg sheets were measured for edge deflection with a cathetometer, then quartered and remeasured. Two postcuring durations were then used, 7.5 and one hr at 177 C; varying cooldown rates after curing were used for other samples, and one set was stored in vacuum at 75 C. Maximum deflections and weight changes were measured periodically at room temperature. Average curvatures, the effect of postcure, and the effect of long-term exposure were determined. Larger panels exhibited cylindrical warping and smaller panels underwent anticlastic warping. The deflections were related to weight changes, i.e. moisture absorption, and the lower the moisture content, the higher the deflection. Relaxation of residual stresses at 75 C was neglibible after 220 days.

Hahn, H. T.↗
NASA NTRS1981

Evaluation of high temperature structural adhesives for extended service

Eight different Ti-6Al-4V surface treatments were investigated for each of 10 candidate resins. Primers (two for each resin) were studied for appropriate cure and thickness and initial evaluation of bond joints began using various combinations of the adhesive resins and surface treatments. Surface failure areas of bonded titanium coupons were analyzed by electron microscopy and surface chemical analysis techniques. Results of surface characterization and failure analysis are described for lap shear bond joints occurring with adhesive systems consisting of: (1) LARC-13 adhesive, Pasa jell surface treatment; (2) LARC-13 adhesive, 10 volt CAA treatment; (3) PPQ adhesive, 10 volt CAA treatment; and (4) PPQ adhesive, 5 volt CAA treatment. The failure analysis concentrated on the 10,000 hr 505K (450 F) exposed specimens which exhibited adhesive failure. Environmental exposure data being generated on the PPQ-10 volt CAA and the LARC-TPI-10 volt CAA adhesive systems is included.

Hill, S. G.↗
NASA NTRS1984

Flight test of a synthetic aperture radar antenna using STEP

To establish confidence in its overall performance, credible information on the synthetic aperture radar antenna's mechanical properties in orbit must be obtained. However, the antenna's size, design, and operating environment make it difficult to simulate operating conditions under 1-g Earth conditions. The Space Technology Experiments Platform (STEP) offers a timely opportunity to mechanically qualify and characterize the antenna design in a representative environment. The proposed experimental configuration would employ a half-system of the full-scale RADARSAT antenna which would be mounted on the STEP platform in the orbiter cargo bay such that it could be deployed and retracted in orbit (as shown in this figure). The antenna would be subjected to typical environmental exposures while an array of targets and sensors on the antenna support structure and reflecting surface are observed and monitored. In particular, the typical environments would include deployment and retraction, dynamic response to vehicle thruster or base exciter inputs, and thermal soak and transient effects upon entering or exiting Earth eclipse. The proposed experiment would also provide generic information on the properties of large space structures in space and on techniques to obtain the desired information.

Zimcik, D. G.↗
NASA NTRS1983

Resin characterization in cured graphite fiber reinforced composites using diffuse reflectance-FTIR

The feasibility of using diffuse reflectance in combination with Fourier transform infrared spectroscopy to obtain information on cured graphite fiber reinforced polymeric matrix resin composites was investigated. Several graphite/epoxy, polysulfone, and polyimide composites exposed to thermal or radiation environments were examined. An experimental polyimide-sulfone adhesive tape was also studied during processing. In each case, significant changes in resin molecular structure was observed due to environmental exposure. These changes in molecular structure were correlated with previously observed changes in material properties providing new insights into material behavior.

Young, P. R.↗
NASA NTRS1984

Matrix Resin Characterization in Cured Graphite Composites Using Diffuse Reflectance-Ftir

The chemical characterization of cured graphite fiber reinforced polymer matrix composites is complicated by the fact that the resins are insoluble and the composites are apaque. Standard analyses which depend either on the ability to dissolve the sample or to detect transmitted radiation are impossible. As a result, data reported on environmentally exposed composites primarily concern macroscopic information such as weight loss or changes in selected mechanical properties. Diffuse reflectance in combination with fourier transform infrared spectroscopy was developed to gain a basic chemical understanding of composite and adhesive behavior. Several composite and adhesive materials were characterized before and after environmental exposure. In each case significant changes in resin molecular structure were observed and correlated with changes in mechanical properties, providing new insights into material performance.

Young, P. R.↗
NASA NTRS1985

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 111 graphite-epoxy spoilers on 737 transport aircraft and related ground based environmental exposure of graphite-epoxy material specimens is covered. Spoilers have been installed on 28 aircraft representing seven major airlines operating throughout the world. An extended flight service evaluation program of 15 years is presently underway. As of December 1984, a total of 2,092, 155 spoiler flight hours and 2,954,814 spoiler landings had been accumulated by this fleet.

Coggeshall, R. L.↗
NASA NTRS1986

Effects of external environments on the short beam shear strength of filament wound graphite/epoxy

Filament wound graphite/epoxy samples were immersed in seawater, deionized water, and toluene at room temperature and 80 deg C for 5, 15, and 43 days, and in methanol at room temperature for 15 and 43 days. The percent weight gains and short beam shear strengths were determined after environmental exposure. Samples immersed in deionized water and seawater had higher percent weight gains than those immersed in toluene at room temperature and 80 deg C. The percent weight gains for samples immersed in methanol at room temperature were comparable to those of deionized water and seawater immersed samples. A comparison of percent decreases in short beam shear strengths could not be made due to a large scatter in data. This may indicate defects in samples due to machining or variations in material properties due to processing.

Penn, B. G.↗
NASA NTRS1986

Lightweight, direct-radiating nickel hydrogen batteries

Two battery module configurations were developed which, in addition to integrating cylindrical nickel hydrogen (NiH2) cells into batteries, provide advances in the means of mounting, monitoring and thermal control of these cells. The main difference between the two modules is the physical arrangement of the cells: vertical versus horizontal. Direct thermal radiation to deep space is accomplished by substituting the battery structure for an exterior spacecraft panel. Unlike most conventional nickel-cadmium (NiCd) and NiH2 batteries, the cells are not tightly packed together; therefore ancillary heat conducting media to outside radiating areas, and spacecraft deck reinforcements for high mass concentration are not necessary. Testing included electrical characterization and a comprehensive regime of environmental exposures. The designs are flexible with respect to quantity and type of cells, orbit altitude and period, power demand profile, and the extent of cell parameter monitoring. This paper compares the characteristics of the two battery modules and summarizes their performance.

Metcalfe, J. R.↗