Interface instabilities in hafnium hydride entrained iron metal matrix composites

The chemical interactions in Fe–HfH 2 metal matrix composites (MMCs) are studied across multiple length scales to elucidate the decomposition of the parent phases and corresponding reaction zone physics during direct current sintering. Fe–HfH 2 composites were synthesized with increasing as-mixed hydride contents of Fe–25% HfH 2 , Fe–40% HfH 2 , Fe–55% HfH 2 , and Fe–70% HfH 2 (all in vol. %) to demonstrate the ability to achieve sintered MMCs with target hydride contents. Samples were probed across multiple length scales through a multi-modal workflow employing x-ray diffraction, scanning electron microscopy and segmentation analysis, and synchrotron techniques including hard x-ray fluorescence mapping and nanoprobe x-ray absorption near-edge structure measurements. Under the selected sintering temperature and pressure conditions, hydrogen evolution is seen to evolve through parallel paths: thermal decomposition from during the transformation of HfH 2 to HfH x<2 and through subsequent reaction with the Fe matrix leading to intermetallic phase formation. Specifically, HfFe and HfFe 2 intermetallic formation accelerates the release of hydrogen with a subsequent HfO 2 phase forming at grain boundaries. For this MMC, the consumption or loss of hydrogen can be considerable in compacts with initial hydride loading of 25%–40% HfH 2 approaching 83% hydrogen loss for the lower volume fraction composites. Increasing the volume fraction of HfH 2 to 70% enhanced the retained hydrogen content to 53% and attributed to the reduced interfacial area intrinsic to the increased HfH 2 loading in this MMC.

36 MATERIALS SCIENCE↗

Atomic structure of different surface terminations of polycrystalline ZnPd

The intermetallic compound ZnPd has been found to have desirable characteristics as a catalyst for the steam reforming of methanol. The understanding of the surface structure of ZnPd is important to optimize its catalytic behavior. However, due to the lack of bulk single-crystal samples and the complexity of characterizing surface properties in the available polycrystalline samples using common experimental techniques, all previous surface science studies of this compound have been performed on surface alloy samples formed through thin-film deposition. In this study, we present findings on the chemical and atomic structure of the surfaces of bulk polycrystalline ZnPd studied by a variety of complementary experimental techniques, including scanning tunneling microscopy (STM), x-ray photoelectron spectroscopy (XPS), low energy electron microscopy (LEEM), photoemission electron microscopy (PEEM), and microspot low-energy electron diffraction ( μ -LEED). These experimental techniques, combined with density functional theory (DFT)-based thermodynamic calculations of surface free energy and detachment kinetics at the step edges, confirm that surfaces terminated by atomic layers composed of both Zn and Pd atoms are more stable than those terminated by only Zn or Pd layers. DFT calculations also demonstrate that the primary contribution to the tunneling current arises from Pd atoms, in agreement with the STM results. The formation of intermetallics at surfaces may contribute to the superior catalyst properties of ZnPd over Zn or Pd elemental counterparts. Published by the American Physical Society 2024

36 MATERIALS SCIENCE↗

Dissimilar metal joining of Ti-6Al-4V and Inconel 625

The dissimilar joining of Ti-6Al-4V and Inconel 625 by using a suitable interlayer shows potential design flexibility by avoiding the brittle intermetallic phases from direct welding. These phases include NiTi , NiTi 2 , and Ni 3 Ti . The objective of this work is to facilitate laser welding of Ti-6Al-4V and Inconel 625 through a vanadium interlayer to form an intermetallic free, strong, and corrosion resistant joint. Vanadium was chosen based on binary phase diagram solubilities, literature, and theoretical CalPhaD calculations in PanDat. Laser welding was systematically explored from based on beam mode, offset, power, and scan speed. Varied parameters include laser power from 325 to 650 watts, laser scan speed from 80 to 160 in/min, and beam offset up to a ¼ of the beam diameter. Parameters were chosen based on previous dissimilar joining research and those found in the literature. Metallography, including optical and scanning electron microscopy, was used to analyze the weld chemical composition, grain structure, and defects through both the fusion and heat affected zones. The results and discussion will examine the relationship between process parameters, microstructure, and observed weld defects. Our findings will not only assess the weldability of vanadium and Inconel 625 but also establish a transferable framework for studying other dissimilar material combinations, providing valuable insights for future research in this field.

36 MATERIALS SCIENCE↗

Towards engineering the growth morphology of anisotropic bicrystals

Eutectic alloys, such as Pb-free Bi-Sn-Ag or Sn-Ag-Cu, are essential for their low melting points in solder joints but suffer from brittle intermetallic phases, reducing reliability. Traditional solder design relies on equilibrium phase diagrams, often neglecting the kinetic influence of crystalline anisotropy during solidification. This study hypothesizes that the energetics at the solid-solid-liquid trijunction dictate crystalline facet selection. Using the Al-Al 3 Ni alloy as a model, this project combines atomistic simulations and experimental methods to understand interfacial energies and develop predictive models. This approach aims to mitigate the negative effects of intermetallics, enhancing component reliability in electronic applications.

36 MATERIALS SCIENCE↗

Upcycling of Mixed Aluminum Alloy Shredder Scrap using Shear Processing

Conservation of critical materials is an increasing area of focus in the Unites States. In 2023, aluminum was added to the US Department of Energy Final Critical Materials List which has spurred public and private research into sustainable management of these resources. Additionally, efficiency in manufacturing and conservation of natural resources are growing concerns with targets to lower global carbon emissions, as primary aluminum alloy production is energy intensive, requiring 14 MWh of electricity plus 0.4 tonnes of CO2 per tonne of Al. Due to these factors, is essential that more sustainable manufacturing methods for aluminum alloys are developed going forward. To this end, much research is ongoing on the topic of more efficient utilization and recovery. However, most of this research still requires primary aluminum in the production process. Here, it will be attempted to bypass the use of primary aluminum and produce useful material recycled from 100% post-consumer scrap. Even considering recent developments in recycling of Al scrap, there is still a large amount of post-consumer scrap that is underutilized due to high impurity content, and that amount will increase significantly as more and more aluminum alloys are utilized in vehicles. This “scrap wave” is expected to cover 80% of the demand for automotive aluminum alloys by 2050 . A challenge to be addressed before the coming scrap wave can be fully utilized is that the tolerance of manufacturing techniques to impurities or off-spec alloy compositions must be increased. Particularly, in 5000-and 6000-series alloys (the most common wrought alloys in durable products), excess iron, copper, and silicon create brittle intermetallics during casting that remain in the extruded microstructure which limit the formability, ductility, and corrosion resistance of the alloy. Concerningly, many of the highest-volume post-consumer aluminum scrap streams such as automotive shredder scrap contain a mix of alloys including both wrought and cast alloys. Their compositions can vary widely depending on geography and the time of year. Because they are mixed, they often contain high content of multiple alloying elements such as Si and Cu in higher concentrations than are found in typical wrought alloys. They may also be contaminated with non-Al alloys from fasteners that get mixed in and often have high content of unwanted elements such as Fe. As a method for utilizing these underused scrap streams that are high in tramp elements, an emerging extrusion technology is being developed at the Pacific Northwest National Laboratory (PNNL) that aims to upcycle 100% post-consumer aluminum scrap directly into extruded components without the addition of primary aluminum . This new technology, called Shear Assisted Processing and Extrusion (ShAPE), is enabling a shift away from today’s recycling paradigm by reaching deeper into lower-value scrap streams, using shredder scrap as the extrusion billet material. Sometimes referred to as Twitch or Tweak, these scrap streams result from shredding and sorting of automobiles, building materials, appliances, and consumer goods. ShAPE combines the linear axis of conventional extrusion with a rotating extrusion die. This rotating die applies large strain to the material during extrusion, which breaks up large impurity-containing intermetallic particles, reducing their deleterious effects. This has been demonstrated for 6063 machining scrap spiked with excess Fe, and Twitch scrap high in Fe, Si and Cu where strength and ductility were retained for both feedstock compositions. Additionally, the extreme plastic deformation during ShAPE enables extrusion of billets with high Si that are too brittle for processing by conventional extrusion. By using 100% post-consumer shedder scrap as feedstock, ShAPE has the potential to slash embodied energy and carbon in extruded components by >80% compared to conventional extrusion of primary aluminum alloys.

Milligan, Brian K.↗

Fabrication studies of Nb3Al superconductors.

Study aimed at developing fabrication techniques for the production of stabilized conductors containing both binary and ternary intermetallics of the Nb-Al system. Processes are described that offer a foundation for practical fabricating techniques suitable for the production of long lengths of stabilized Nb3Al superconductor. Once the parameters are optimized, it is conceivable that multistrand twisted composites of both binary and ternary intermetallics should become feasible.

Worzala, F. J.↗

Method of fabricating a twisted composite superconductor

A method of producing a twisted, stabilized wire or tube superconductor which can be used to wind electromagnets, armatures, rotors, field windings for motors and generators, and other magnetic devices which use a solenoid, toroidal, or other type winding is reported. At least one groove is formed along the length of a wire substrate which is then twisted into a helix and a layer of intermetallic superconducting material is formed in the groove. This layer can be formed by depositing the desired intermetallic compound into the groove or by diffusing one component of the superconductor into the groove formed in a substrate composed of the other component. The superconductor prepared by this method comprises a non-superconductor wire twisted into the shape of a helix, having at least one groove containing a layer of superconductor material along the length of the wire.

Brown, G. V.↗

Directionally solidified pseudo-binary eutectics of Ni-Cr-(Hf, Zr)

A pseudo-binary eutectic, in which the intermetallic Ni7Hf2 reinforces the Ni-Cr solid solution phase, was previously predicted in the Ni-Cr-Hf system by a computer analysis. The experimental determination of pseudo binary eutectic compositions and the directional solidification of the Ni-Cr-Hf, Zr, and Ni-Cr-Zr eutectic alloys are discussed. To determine unknown eutectics, chemical analyses were made of material bled from near eutectic ingots during incipient melting. Nominal compositions in weight percent of Ni-18.6Cr-24.0HF, Ni19.6Cr-12.8Zr-2.8Hf, and Ni-19.2Cr-14.8Zr formed aligned pseudo-binary eutectic structures. The melting points were about 1270 C. The reinforcing intermetallic phases were identified as noncubic (Ni,Cr)7Hf2 and (Ni,Cr)7(Hf,Zr)2, and face centered cubic (Ni,Cr)5Zr. The volume fraction of the reinforcing phases were about 0.5.

Kim, Y. G.↗

Superconducting compounds and alloys research

Resistivity measurements as a function of temperature were performed on alloys of the binary material system In sub(1-x) Bi sub x for x varying between 0 and 1. It was found that for all single-phase alloys (the pure elements, alpha-In, and the three intermetallic compounds) at temperatures sufficiently above the Debye-temperature, the resistivity p can be expressed as p = a sub o T(n), where a sub o and n are composition-dependent constants. The same exponential relationship can also be applied for the sub-system In-In2Bi, when the two phases are in compositional equilibrium. Superconductivity measurements on single and two-phase alloys can be explained with respect to the phase diagram. There occur three superconducting phases (alpha-In, In2Bi, and In5Bi3) with different transition temperatures in the alloying system. The magnitude of the transition temperatures for the various intermetallic phases of In-Bi is such that the disappearance or occurrence of a phase in two component alloys can be demonstrated easily by means of superconductivity measurements.

Otto, G.↗

Recrystallization and grain growth in NiAl

Aluminide intermetallics, because of their strength, microstructural stability, and oxidation resistance at elevated temperatures, represent potential structural materials for use in advanced energy conversion systems. This inherent potential of the intermetallics can currently not be realized in connection with the general brittleness of the materials under ambient conditions. It is pointed out, however, that brittleness is not an inherent characteristic. Single crystals are ductile and polycrystals may be, too, if their grains are fine enough. The present investigation is concerned with an approach for reducing material brittleness, taking into account thermal-mechanically induced grain refinement in NiAl, a B2 aluminide which melts at 1638 C and which retains complete order to its melting point. Attention is given to the kinetics of recrystallization and grain growth of warm-worked, nickel-rich material.

Haff, G. R.↗

New eutectic alloys and their heats of transformation

Eutectic compositions and congruently melting intermetallic compounds in binary and multicomponent systems among common elements such as Al, Ca, Cu, Mg, P, Si, and Zn may be useful for high temperature heat storage. In this work, heats of fusion of new multicomponent eutectics and intermetallic phases are reported, some of which are competitive with molten salts in heat storage density at high temperatures. The method used to determine unknown eutectic compositions combined results of differential thermal analysis, metallography, and microprobe analysis. The method allows determination of eutectic compositions in no more than three steps. The heats of fusion of the alloys were measured using commercial calorimeters, a differential thermal analyzer, and a differential scanning calorimeter.

Farkas, D.↗

Effect of boron on tensile properties of B2 BeAl

Small additions of boron were shown to improve the room temperature ductility of the intermetallic compound Ni3Al. Boron is believed to segregate to the gain boundaries and strengthen them, allowing the inheret ductility of the grains to be achieved. The present study was undertaken to see if boron has a similar effect on the low temperature tensile properties of the equiatomic intermetallic compound FeAl. A binary alloy without boron is compared with an alloy containing 0.78 at % B (0.2 wt %) B, by tensile testing over the temperature range of 300 K to 640 K. Both alloys were processed by powder metallurgy. Results showed that 0.78 at % B addition to FeAl does indeed change the room temperature fracture mode from intergranular to transgranular, suggesting a strengthening of grain boundaries. The alloy containing boron is, however, still brittle at room temperature. A slight decrease in the ductile to brittle transition temperature is, nevertheless, observed. In addition a significant increase in strength of the alloy is observed with boron addition.

Crimp, M.↗

Status and prognosis for alternative engine materials

The current state of research and development of new materials for advanced aircraft engines is reviewed. The advantages and disadvantages of intermetallic compounds and refractory metals as replacements for today's nickel-base alloys are discussed along with some results of research directed at overcoming some of the problems which restrict their application. It is concluded that continuous fiber reinforced intermetallic matrix composites offer one of the best chances for success. However, major technical barriers still exist, especially in the development of suitable fibers. The introduction of these materials into aircraft engines is expected to take in excess of 5 to 10 years.

Stephens, Joseph R.↗

Theoretical analysis of compatibility of several reinforcement materials with NiAl and FeAl matrices

Several potential reinforcement materials were assessed for their chemical, coefficient of thermal expansion (CTE), and mechanical compatibility with the intermetallic matrices based on NiAl and FeAl. Among the ceramic reinforcement materials, Al2O3, TiC, and TiB2, appear to be the optimum choices for NiAl and FeAl matrices. However, the problem of CTE mismatch with the matrix needs to be solved for these three reinforcement materials. Beryllium-rich intermetallic compounds can be considered as potential reinforcement materials provided suitable reaction barrier coatings can be developed for these. Based on preliminary thermodynamic calculations, Sc2O3 and TiC appear to be suitable as reaction barrier coatings for the beryllides. Several reaction barrier coatings are also suggested for the currently available SiC fibers.

Misra, Ajay K.↗

Status and prognosis for alternative engine materials

The current state of research and development of new materials for advanced aircraft engines is reviewed. The advantages and disadvantages of intermetallic compounds and refractory metals as replacements for today's nickel-base alloys are discussed along with some results of research directed at overcoming some of the problems which restrict their application. It is concluded that continuous fiber reinforced intermetallic matrix composites offer one of the best chances for success. However, major technical barriers still exist, especially in the development of suitable fibers. The introduction of these materials into aircraft engines is expected to take in excess of 5 to 10 years.

Stephens, Joseph R.↗

Up-and-coming IMCs

While the good oxidation and environmental resistance, high melting points, and comparatively low densities of such ordered intermetallics as Ti3Al, NiAl, FeAl, and NbAl3 render them good candidates for advanced aerospace structures, their poor toughness at low temperatures and low strength at elevated temperatures have prompted the development of fiber-reinforced intermetallic-matrix composites (IMCs) with more balanced characteristics. Fabrication methods for continuous-fiber IMCs under development include the P/M 'powder cloth' method, the foil/fiber method, and thermal spraying. The ultimate success of IMCs depends on fibers truly compatible with the matrix materials.

Bowman, Randy↗

Preliminary investigation of a NiAl composite prepared by cryomilling

An attempt has been made to improve the high temperature mechanical strength of the B2 cubic crystal structure intermetallic NiAl by dispersion strengthening. Prealloyed Ni-51 at. pct Al was cryomilled with a Y2O3 addition to form an yttria dispersoid within the intermetallic matrix. Following milling, the powder was hot extruded to full density and machined into test coupons. Compression testing between 1200 and 1400 K indicated that the cryogenic process yielded the strongest NiAl based material tested to date. Creep resistance was six times better than NiAl and twice that of a NiAl particulate composite containing 10 vol pct TiB2. Surprisingly, transmission electron microscopy revealed that the second phase was inhomogeneously distributed. Furthermore, X-ray analysis indicated that the second phase was not Y2O3 but rather AlN.

Whittenberger, J. Daniel↗