Test conditions and results are reported for various coatings on a 1 percent zirconium columbium alloy at a temperature of 2000 deg F. Molybdenum silicide over molybdenum is most effective coating, tin-aluminum coating is adequately protective, chromium-molybdenum silicides are not protective.
Thermodynamic properties of carbon in molybdenum and tungsten at solubility limit
Rhenium alloying effect on room temperature ductility of Cr, Mo and W, measuring lattice parameters by Debye-Scherer method
Weldability of tungsten base alloys and elevated temperature stability
Post weld annealing for stabilizing tungsten alloy weld structure
Fast neutron reactivity effects of reactor materials measured in thermal uranyl fluoride-water-solution reactor
Tensile and stress-rupture tests were conducted on wires of W-Hf-C, W-Re-Hf-C, ASTAR 811C (a tantalum alloy), and B-88 (a columbium alloy) at room temperature, 1093 C (2000 F), and 1204 C (2200 F). Metallographic examinations were also made of the wire microstructure after testing. Ultimate tensile strength values up to 2170 meganewtons per square meter (314000 psi) at 1093 C (2000 F) and 1940 meganewtons per square meter (281 000 psi) at 1204 C (2200 F) were obtained for W-Re-Hf-C wire. The best strength values obtained for a 100-hour rupture life were, 1410 meganewtons per square meter (205 000 psi) at 1093 C (2000 F) and 910 meganewtons per square meter (132 000 psi) at 1240 C (2200 F) for W-Re-Hf-C wire. The properties obtained suggested that the wires studied showed promise as potential fiber reinforcement in the 1093 to 1204 C (2000 to 2200 F) temperature range.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
The effects of some materials variables on the irradiation performance of fuel pins for a lithium-cooled space power reactor design concept were examined. The variables studied were UN fuel density, fuel composition, and cladding alloy. All pins were irradiated at about 990 C in a thermal neutron environment to the design fuel burnup. An 85-percent dense UN fuel gave the best overall results in meeting the operational goals. The T-111 cladding on all specimens was embrittled, possibly by hydrogen in the case of the UN fuel and by uranium and oxygen in the case of the UO2 fuel. Tests with Cb-1Zr cladding indicate potential use of this cladding material. The UO2 fueled specimens met the operational goals of less than 1 percent cladding strain, but other factors make UO2 less attractive than low-density UN for the contemplated space power reactor use.
The alloys of niobium and tantalum are attractive from a strength and compatibility viewpoint for high operating temperatures required in materials for fuel cladding, liquid metal transfer, and heat pipe applications in space power systems that will supply from 100 kWe to multi-megawatts for advanced space systems. To meet the system requirements, operating temperatures ranging from 1100 to 1600 K have been proposed. Expected lives of these space power systems are from 7 to 10 yr. A program is conducted at NASA Lewis to determine the effects of long-term, high-temperature exposure on the microstructural stability of several commercial tantalum and niobium alloys. Variables studied in the investigation include alloy composition, pre-age annealing temperature, aging time, temperature, and environment (lithium or vacuum), welding, and hydrogen doping. Alloys are investigated by means of cryogenic bend tests and tensile tests. Results show that the combination of tungsten and hafnium or zirconium found in commercial alloys such as T-111 and Cb-752 can lead to aging embrittlement and increased susceptibility to hydrogen embrittlement of ternary and more complex alloys. Modification of alloy composition helps to eliminate the embrittlement problem.
The alloys of niobium and tantalum are attractive from a strength and compatibility viewpoint for high operating temperatures required in materials for fuel cladding, liquid metal transfer, and heat pipe applications in space power systems that will supply from 100 kWe to multi-megawatts for advanced space systems. To meet the system requirements, operating temperatures ranging from 1100 to 1600 K have been proposed. Expected lives of these space power systems are from 7 to 10 yr. A program is conducted at NASA Lewis to determine the effects of long-term, high-temperature exposure on the microstructural stability of several commercial tantalum and niobium alloys. Variables studied in the investigation include alloy composition, pre-age annealing temperature, aging time, temperature, and environment (lithium or vacuum), welding, and hydrogen doping. Alloys are investigated by means of cryogenic bend tests and tensile tests. Results show that the combination of tungsten and hafnium or zirconium found in commercial alloys such as T-111 and Cb-752 can lead to aging embrittlement and increased susceptibility to hydrogen embrittlement of ternary and more complex alloys. Modification of alloy composition helps to eliminate the embrittlement problem.
Creep-rupture and tensile tests have been used to evaluate thoriated W-wire reinforced Nb-1 percent Zr alloy matrix composites fabricated via arc-spray monotape technique. A significant creep strength enhancement was observed over the unreinforced matrix alloy while matrix integrity was maintained; the fiber/matrix interface phase is noted to be a strong and ductile W/Nb alloy, which is formed due to the mutual solubility of the constituent metals. High strength, toughness, and thermal stability are demonstrated by this material system, which is also resistant to liquid alkali metal corrosion.
The space shuttle orbiter s reaction control system (RCS) is a series of small thrusters that use hypergolic fuels to orient the orbiter in space. The RCS thrusters are constructed from a special niobium-based alloy -- the C-103. This alloy retains excellent mechanical properties from cryogenic temperature all the way up to 2,500 F (1,370 C). C-103 is susceptible to rapid oxidation at elevated temperatures. The authors have developed two methods to repair damaged R512a coatings on C-103. For the first repair technique, metal foundries, semiconductor manufacturers, and many other industries have developed and routinely use coatings that can easily be painted on metal to protect it from corrosion, including oxidation, to temperatures in excess of 2,500 F (1,370 C). This first repair technique is considered somewhat temporary. The second repair technique is based on using the native coating material of the RCS nozzles. the chipped area is ground out and a "green" R512a coating is applied to the repair area. Both repair techniques can be applied for moderate protection until the permanent laser-repair technique is available to the repair area.
Heat pipe life tests have seldom been conducted on a systematic basis. Typically, one or more heat pipes are built and tested for an extended period at a single temperature with simple condenser loading. Results are often reported describing the wall material, working fluid, test temperature, test duration, and occasionally the nature of any failure. Important information such as design details, processing procedures, material assay, power throughput, and radial power density are usually not mentioned. We propose to develop methods to generate carefully controlled data that conclusively establish heat pipe operating life with material-fluid combinations capable of extended operation. The test approach detailed in this Technical Publication will use 16 Mo-44.5%Re alloy/sodium heat pipe units that have an approximate12-in length and 5/8-in diameter. Two specific test series have been identified: (1) Long-term corrosion rates based on ASTM-G-68-80 (G-series) and (2) corrosion trends in a cross-correlation sequence at various temperatures and mass fluences based on a Fisher multifactor design (F-series). Evaluation of the heat pipe hardware will be performed in test chambers purged with an inert purified gas (helium or helium/argon mixture) at low pressure (10-100 torr) to provide thermal coupling between the heat pipe condenser and calorimeter. The final pressure will be selected to minimize the potential for voltage breakdown between the heat pipe and radio frequency (RF) induction coil (RF heating is currently the planned method of powering the heat pipes). The proposed calorimeter is constructed from a copper alloy and relies on a laminar flow water-coolant channel design to absorb and transport energy
A series of 16 Mo-44.5%Re alloy/sodium heat pipes will be experimentally tested to examine heat pipe aging. To support this evaluation, an environmental test chamber and a number of auxiliary subsystems are required. These subsystems include radio frequency (RF) power supplies/inductive coils, recirculation water coolant loops, and chamber gas conditioning. The heat pipes will be grouped, based on like power and gas mixture requirements, into three clusters of five units each, configured in a pentagonal arrangement. The highest powered heat pipe will be tested separately. Test chamber atmospheric purity is targeted at <0.3 ppb oxygen at an approximate operating pressure of 76 torr (.1.5 psia), maintained by active purification (oxygen level is comparable to a 10(exp -6) torr environment). Treated water will be used in two independent cooling circuits to remove .85 kW. One circuit will service the RF hardware while the other will maintain the heat pipe calorimetry. Initial procedures for the startup and operation of support systems have been identified. Each of these subsystems is outfitted with a variety of instrumentation, integrated with distributed real-time controllers and computers. A local area network provides communication between all devices. This data and control network continuously monitors the health of the test hardware, providing warning indicators followed by automatic shutdown should potentially damaging conditions develop. During hardware construction, a number of checkout tests.many making use of stainless steel prototype heat pipes that are already fabricated.will be required to verify operation.
With the selection of a gas-cooled reactor, this heat pipe accelerated life test activity was closed out and its resources redirected. The scope of this project was to establish the long-term aging effects on Mo-44.5%Re sodium heat pipes when subjected to space reactor temperature and mass fluences. To date, investigators have demonstrated heat pipe life tests of alkali metal systems up to .50,000 hours. Unfortunately, resources have not been available to examine the effect of temperature, mass fluence, or impurity level on corrosion or to conduct post-test forensic examination of heat pipes. The key objective of this effort was to establish a cost/time effective method to systematically test alkali metal heat pipes with both practical and theoretical benefits. During execution of the project, a heat pipe design was established, a majority of the laboratory test equipment systems specified, and operating and test procedures developed. Procurements for the heat pipe units and all major test components were underway at the time the stop work order was issued. An extremely important outcome was the successful fabrication of an annular wick from Mo-5%Re screen (the single, most difficult component to manufacture) using a hot isostatic pressing technique. This Technical Publication (TP) includes specifics regarding the heat pipe calorimeter water-cooling system, vendor design for the radio frequency heating system, possible alternative calorimeter designs, and progress on the vanadium equilibration technique. The methods provided in this TP and preceding project documentation would serve as a good starting point to rapidly implement an accelerated life test. Relevant test data can become available within months, not years, and destructive examination of the first life test heat pipe might begin within 6 months of test initiation. Final conclusions could be drawn in less than a quarter of the mission duration for a long-lived, fission-powered, deep space probe.